Tribological Properties and Wear Mechanisms of NiCr–Al₂O₃–SrSO₄–Ag Self-Lubricating Composites at Elevated Temperatures

NiCr–Al₂O₃–SrSO₄–Ag self-lubricating composites were prepared by powder metallurgy method and the tribological properties of composites were evaluated by a ball-on-disk tribometer against alumina ball at wide temperature range from the room temperature to 1,000 °C in air. The linear coefficient of thermal expansion was evaluated for investigation of thermal stability of composites. The tribo-chemical reaction films formed on the rubbing surfaces and their effects on the tribological properties of composites at different temperatures were addressed according to the surface characterization by SEM, XRD, and XPS. The results show that the NiCr–Al₂O₃ composite with addition of 10 wt% SrSO₄ and 10 wt% Ag exhibits satisfying friction and wear properties over the entire temperature range from room temperature to 1,000 °C. The composition of the tribo-layers on the worn surfaces of the composites is varied at different temperatures. The synergistic lubricating effect of SrAl₄O₇, Ag, and NiCr₂O₄ lubricating films formed on worn surfaces were identified to reduce the friction coefficient and wear rate from room temperature to 800 °C. Meanwhile, at 1,000 °C, the SrCrO₄ and NiAl₂O₄ was formed on the worn surfaces during sliding process, combining with the NiCr₂O₄, Al₂O₃, Cr₂O₃, Ag, and Ag₂O, which play an important role in the formation of a continuous lubricating film on the sliding surface.