Effect of hybrid nanofillers on the thermal, mechanical, and physical properties of polypropylene composites

In this study, the effect of single and hybrid nanofillers on the thermal, mechanical, and physical properties of polypropylene composites were carried out. This nanocomposite was compounded using two-roll mill mixing method and the filler content was fixed at 4 vol % loading. The single filler used is synthetic diamond (SD), boron nitride (BN), and carbon nanotube (MWNT). The hybrid system was composed by addition of MWNT into single SD and BN. The prepared samples were characterized by thermal properties, tensile and flexural, and these results were supported by the morphology, void content, and melt flow index values. The result showed that the hybrid composite with combination of BN and SD with MWNT indicate higher thermal conductivity and thermal stability and lower thermal expansion. However, no significant improvements in tensile and flexural strengths were observed due to large formation of agglomeration as being captured by SEM micrographs. Furthermore, the existence of higher percent void content suggests low adhesion and poor compatibility between hybrid filler and matrix. This caused detrimental effect of strength of hybrid composites rather than single filler composites.