Effect of silicon carbide dispersion on the microwave absorbing properties of silicon carbide-epoxy composites in 2–40 GHz
Erschienen in: Journal of Polymer Research | Ausgabe 4/2016
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
In this study, silicon carbide powders were manufactured successfully by the method of preheating combustion synthesis in nitrogen atmosphere where it was introduced into an epoxy resin to produce a microwave absorber. The structure of the silicon carbide was characterized by using X-ray diffraction (XRD) and scanning electron microscopy (SEM). Composite based on the various loadings of silicon carbide and epoxy resin specimens were prepared and the reflection losses of these composite samples were studied using the free space method. Based on the microwave measurements, microwave absorber specimens of silicon carbide with thermal plastic resin at frequencies between 2 and 18 and 18–40 GHz could be obtained from a matching thickness of 2.0 mm by controlling the content of silicon carbide.