03.01.2021 | ORIGINAL ARTICLE

Experimental study on surface integrity changes during turning-ultrasonic impact of nickel alloy 718

verfasst von: Changfeng Yao, Zheng Zhou, Yu Zhao, Liang Tan, Minchao Cui, Yang Wang

Erschienen in: The International Journal of Advanced Manufacturing Technology | Ausgabe 5-6/2021

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Ultrasonic impact strengthening is a kind of “no cutting” processing technology. It is widely used in surface strengthening of mechanical parts. In this research, the surface integrity changes the mechanism in the composite process of turning-ultrasonic impacting of nickel alloy 718 was studied and analyzed. The turning surface quality was significantly improved when treated with the same set of ultrasonic impact parameters due to the extrusion and impacting of ultrasonic impact head. The average value of surface roughness Ra was about 0.2 μm. The profile valley effective radius was about 5 μm. The value of surface stress concentration factor was within a small range from 1.07 to 1.11. During the process of ultrasonic impact, severe plastic deformation occurred in the surface material, the dislocation density increased rapidly, and the grains were refined. This resulted in the improvement of the mechanical properties of the surface material. The axial residual stress was around − 1800 MPa, and its influence depth increased by nearly 10 times. The maximum value of surface microhardness was 593.28 HV, and its influence depth was 120 μm. The distribution of residual stress and microhardness along the depth direction has been characterized by cosine decay function and exponential decay function. The thickness of the plastic deformation layer increased from 3 to about 19 μm. EBSD test showed that the grain size decreased by nearly 90%. In general, the surface integrity was significantly improved after ultrasonic impacting treatment regardless of the initial turning surface conditions.

Vorheriger Artikel Parameterized multipoint-line analytical modeling of a mobile heat source for thermal field prediction in laser beam welding

Nächster Artikel A novel method with Newton polynomial-Chebyshev nodes for milling stability prediction

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Zhang K, Liu Y, Liu S, Zhang X, Qian B, Zhang C, Tu S (2019) Coordinated bilateral ultrasonic surface rolling process on aero-engine blades. Int J Adv Manuf Technol 105:4415–4428CrossRef

Lu LX, Sun J, Li L, Xiong QC (2016) Study on surface characteristics of 7050-T7451 aluminum alloy by ultrasonic surface rolling process. Int J Adv Manuf Technol 87:2533–2539. https://doi.org/10.1007/s00170-016-8659-4CrossRef

Li F, Zhao B, Lan S, Feng Z (2020) Experiment and simulation of the effect of ultrasonic rolling on the surface properties of Ti-6Al-4V. Int J Adv Manuf Technol 106:1893–1900. https://doi.org/10.1007/s00170-019-04648-4CrossRef

Feng Y, Hu S, Wang D, Cui L (2016) Formation of short crack and its effect on fatigue properties of ultrasonic peening treatment S355 steel. Mater Des 89:507–515. https://doi.org/10.1016/j.matdes.2015.10.009CrossRef

Xu X, Liu D, Zhang X, Liu C, Liu D, Zhang W (2019) Influence of ultrasonic rolling on surface integrity and corrosion fatigue behavior of 7B50-T7751 aluminum alloy. Int J Fatigue 125:237–248. https://doi.org/10.1016/j.ijfatigue.2019.04.005CrossRef

Hu S, Guo C, Wang D, Wang Z, Huang C (2018) Finite element analysis of residual stress evolution with multiple impacts on one point in ultrasonic impact treatment process. Proc Inst Mech Eng Part B J Eng Manuf 232:1201–1211. https://doi.org/10.1177/0954405416666894CrossRef

Ohta T (2018) Numerical analysis of effect of pin tip radius on residual stress distribution in ultrasonic impact treatment. Mater Trans 59:656–662. https://doi.org/10.2320/matertrans.P-M2018805CrossRef

Yin D, Wang D, Li W, Li X, Zhang H, Naher S (2017) Development of a new 3D model for the prediction of residual stress and fracture behaviour in Ti-6Al-4V after ultrasonic peening treatment. J Mater Process Technol 247:29–39. https://doi.org/10.1016/j.jmatprotec.2017.03.033CrossRef

Zhang M, Liu Z, Deng J, Yang M, Dai Q, Zhang T (2019) Optimum design of compressive residual stress field caused by ultrasonic surface rolling with a mathematical model. Appl Math Model 76:800–831. https://doi.org/10.1016/j.apm.2019.07.009MathSciNetCrossRefMATH

10.

Wang F, Men X, Liu Y, Fu X (2020) Experiment and simulation study on influence of ultrasonic rolling parameters on residual stress of Ti-6Al-4V alloy. Simul Model Pract Theory 104:102121. https://doi.org/10.1016/j.simpat.2020.102121CrossRef

11.

Zhao J, Liu Z (2016) Investigations of ultrasonic frequency effects on surface deformation in rotary ultrasonic roller burnishing Ti-6Al-4V. Mater Des 107:238–249. https://doi.org/10.1016/j.matdes.2016.06.024CrossRef

12.

Ao N, Liu D, Xu X, Zhang X, Liu D (2019) Gradient nanostructure evolution and phase transformation of α phase in Ti-6Al-4V alloy induced by ultrasonic surface rolling process. Mater Sci Eng A 742:820–834. https://doi.org/10.1016/j.msea.2018.10.098CrossRef

13.

Liu D, Liu D, Zhang X, Liu C, Ni A (2018) Surface nanocrystallization of 17-4 precipitation-hardening stainless steel subjected to ultrasonic surface rolling process. Mater Sci Eng A 726:69–81. https://doi.org/10.1016/j.msea.2018.04.033CrossRef

14.

Cao XJ, Pyoun YS, Murakami R (2010) Fatigue properties of a S45C steel subjected to ultrasonic nanocrystal surface modification. Appl Surf Sci 256:6297–6303. https://doi.org/10.1016/j.apsusc.2010.04.007CrossRef

15.

Ting W, Dongpo W, Gang L, Gong B, Song N (2008) Investigations on the nanocrystallization of 40Cr using ultrasonic surface rolling processing. Appl Surf Sci 255:1824–1829. https://doi.org/10.1016/j.apsusc.2008.06.034CrossRef

16.

Liu D, Liu D, Zhang X, Ma A, Liu C (2020) Microstructural evolution mechanisms in rolled 17-4PH steel processed by ultrasonic surface rolling process. Mater Sci Eng A 773 https://doi.org/10.1016/j.msea.2019.138720

17.

Ren Z, Lai F, Qu S, Zhang Y, Li X, Yang C (2020) Effect of ultrasonic surface rolling on surface layer properties and fretting wear properties of titanium alloy Ti5Al4Mo6V2Nb1Fe. Surf Coatings Technol 389:125612. https://doi.org/10.1016/j.surfcoat.2020.125612CrossRef

18.

Li G, Qu SG, Pan YX, Li XQ (2016) Effects of the different frequencies and loads of ultrasonic surface rolling on surface mechanical properties and fretting wear resistance of HIP Ti–6Al–4V alloy. Appl Surf Sci 389:324–334. https://doi.org/10.1016/j.apsusc.2016.07.120CrossRef

19.

Ao N, Liu D, Zhang X, Liu C, Yang J, Liu D (2019) Surface nanocrystallization of body-centered cubic beta phase in Ti–6Al–4V alloy subjected to ultrasonic surface rolling process. Surf Coatings Technol 361:35–41. https://doi.org/10.1016/j.surfcoat.2019.01.045CrossRef

20.

Dutta RK, Malet L, Gao H, Hermans M, Godet S, Richardson I (2015) Formation of nanostructures in severely deformed high-strength steel induced by high-frequency ultrasonic impact treatment. Metall Mater Trans A Phys Metall Mater Sci 46:813–830. https://doi.org/10.1007/s11661-014-2658-6CrossRef

21.

Liu Y, Xue G, Zhao X (2017) Strain-induced gradient crystalline evolution mechanism of Ti-6.5Al-3.5Mo-1.5Zr-0.3Si during ultrasonic impacting and rolling process. Micro Nano Lett 12:304–307. https://doi.org/10.1049/mnl.2016.0788CrossRef

22.

Liu C, Liu D, Zhang X, Yu S, Zhao W (2017) Effect of the ultrasonic surface rolling process on the fretting fatigue behavior of Ti-6Al-4V alloy. Materials (Basel) 10:833. https://doi.org/10.3390/ma10070833CrossRef

23.

Zhao W, Liu D, Zhang X, Zhou Y, Zhang R, Zhang H, Ye C (2019) Improving the fretting and corrosion fatigue performance of 300M ultra-high strength steel using the ultrasonic surface rolling process. Int J Fatigue 121:30–38. https://doi.org/10.1016/j.ijfatigue.2018.11.017CrossRef

24.

Zhao X, Xue G, Liu Y (2017) Gradient crystalline structure induced by ultrasonic impacting and rolling and its effect on fatigue behavior of TC11 titanium alloy. Results Phys 7:1845–1851. https://doi.org/10.1016/j.rinp.2017.05.026CrossRef

25.

Li G, Qu S, Xie M, Ren Z, Li X (2017) Effect of multi-pass ultrasonic surface rolling on the mechanical and fatigue properties of HIP Ti-6Al-4V alloy. Materials (Basel) 10. https://doi.org/10.3390/ma10020133

26.

Panin AV, Kazachenok MS, Kozelskaya AI, Balokhonov RR, Romanova VA, Perevalova OB, Yu P (2017) The effect of ultrasonic impact treatment on the deformation behavior of commercially pure titanium under uniaxial tension. Mater Des 117:371–381. https://doi.org/10.1016/j.matdes.2017.01.006CrossRef

27.

Liu C, Liu D, Zhang X, Liu D, Ma A, Ni A, Xu X (2019) Improving fatigue performance of Ti-6Al-4V alloy via ultrasonic surface rolling process. J Mater Sci Technol 35:1555–1562. https://doi.org/10.1016/j.jmst.2019.03.036CrossRef

28.

Wang C, Xu G, Zeng L, Tang Z, Zhang X, Liang T (2020) Enhanced corrosion behavior and mechanical properties of Al-Zn-Mg-Cu sheet alloy by ultrasonic surface rolling treatment. Metall Mater Trans A Phys Metall Mater Sci 51:1967–1971. https://doi.org/10.1007/s11661-020-05685-5CrossRef

29.

Ao N, Liu D, Liu C, Zhang X, Liu D (2018) Face-centered titanium induced by ultrasonic surface rolling process in Ti-6Al-4V alloy and its tensile behavior. Mater Charact 145:527–533. https://doi.org/10.1016/j.matchar.2018.09.004CrossRef

30.

Arola D (2009) Surface texture and the stress concentration factor for FRP components with holes. J Compos Mater 37:1439–1460. https://doi.org/10.1177/002199803034462CrossRef

Titel: Experimental study on surface integrity changes during turning-ultrasonic impact of nickel alloy 718
verfasst von: Changfeng Yao
Zheng Zhou
Yu Zhao
Liang Tan
Minchao Cui
Yang Wang
Publikationsdatum: 03.01.2021
Verlag: Springer London
Erschienen in: The International Journal of Advanced Manufacturing Technology / Ausgabe 5-6/2021
Print ISSN: 0268-3768
Elektronische ISSN: 1433-3015
DOI: https://doi.org/10.1007/s00170-020-06503-3

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 5-6/2021

Announcement of B. John Davies Prize for the best paper published in IJAMT in 2019

Milling stability prediction based on the hybrid interpolation scheme of the Newton and Lagrange polynomials

Multi-objective robust evolutionary optimization of the boring process of AISI 4130 steel

Biomimetic strategies for fabricating musculoskeletal tissue scaffolds: a review

Springback control and plastic deformation of metal plates with large curvature in heat-assisted incremental bending process

STEP/STEP-NC-compliant manufacturing information of 3D printing for FDM technology

Premium Partner

Marktübersichten