Fabrication of carbon nanofiber by pyrolysis of freeze-dried cellulose nanofiber

verfasst von: Ehsan Jazaeri, Liyuan Zhang, Xungai Wang, Takuya Tsuzuki

Erschienen in: Cellulose | Ausgabe 6/2011

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

The possibility of fabricating carbon nanofibers from cellulose nanofibers was investigated. Cellulose nanofiber of ~50 nm in diameter was produced using ball milling in an eco-friendly manner. The effect of the drying techniques of cellulose nanofibers on the morphology of carbon residue was studied. After pyrolysis of freeze-dried cellulose nanofibers below 600 °C, amorphous carbon fibers of ~20 nm in diameter were obtained. The pyrolysis of oven-dried precursors resulted in the loss of original fibrous structures. The different results arising from the two drying techniques are attributed to the difference in the spatial distance between cellulose nanofiber precursors.

Vorheriger Artikel Effect of alkylimidazolium based ionic liquids on the structure of UV-irradiated cellulose

Nächster Artikel An improved model for the kinetic description of the thermal degradation of cellulose

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Cao Y, Tan HM (2002) Effects of cellulase on the modification of cellulose. Carbohydr Res 337:1291–1296CrossRef

Ishida O, Kim DY, Kuga S, Nishiyama Y, Brown RM (2004) Microfibrillar carbon from native cellulose. Cellulose 11:475–480CrossRef

Khezami L, Chetouani A, Taouk B, Capart R (2005) Production and characterisation of activated carbon from wood components in powder: cellulose, lignin, xylan. Powder Technol 157:48–56CrossRef

Kim DY, Nishiyama Y, Wada M, Kuga S (2001) Graphitization of highly crystalline cellulose. Carbon 39:1051–1056CrossRef

Nogi M, Kurosaki F, Yano H, Takano M (2010) Preparation of nanofibrillar carbon from chitin nanofibers. Carbohydr Polym 81:919–924CrossRef

Oh SY, Yoo DI, Shin Y, Kim HC, Kim HY, Chung YS, Park WH, Youk JH (2005) Crystalline structure analysis of cellulose treated with sodium hydroxide and carbon dioxide by means of X-ray diffraction and FTIR spectroscopy. Carbohydr Res 340:2376–2391CrossRef

Sekiguchi Y, Frye JS, Shafizadeh F (1983) Structure and formation of cellulosic chars. J Appl Polym Sci 28(11):3513–3525CrossRef

Sevilla M, Fuertes AB (2010) Graphitic carbon nanostructures from cellulose. Chem Phys Lett 490:63–68CrossRef

Shin S, Jang J, Yoon SH, Mochida IA (1997) Study on the effect of heat treatment on functional groups of pitch based activated carbon fiber using FTIR. Carbon 35(12):1739–1743CrossRef

Tang MM, Bacon R (1964) Carbonization of cellulose fibers-I low temperature pyrolysis. Carbon 2(3):211–214CrossRef

Tran PA, Zhang LJ, Webster TJ (2009) Carbon nanofibers and carbon nanotubes in regenerative medicine. Adv Drug Deliv Rev 62:667CrossRef

Uchida T, Anderson DP, Minus ML, Kumar S (2006) Morphology and modulus of vapor grown carbon nano fibers. J Mater Sci 41:5851–5856CrossRef

Yoshino K, Matsuoka R, Nogami K, Yamanaka S, Watanabe K, Takahashi M, Honma M (1990) Graphite film prepared by pyrolysis of bacterial cellulose. J Appl Phys 68:1720–1725CrossRef

Zhang L, Tsuzuki T, Wan X (2010) Preparation and characterization on cellulose nanofiber film. Mater Sci Forum 654–656:1760–1763CrossRef

Titel: Fabrication of carbon nanofiber by pyrolysis of freeze-dried cellulose nanofiber
verfasst von: Ehsan Jazaeri
Liyuan Zhang
Xungai Wang
Takuya Tsuzuki
Publikationsdatum: 01.12.2011
Verlag: Springer Netherlands
Erschienen in: Cellulose / Ausgabe 6/2011
Print ISSN: 0969-0239
Elektronische ISSN: 1572-882X
DOI: https://doi.org/10.1007/s10570-011-9596-x

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Technik"

Springer Professional "Wirtschaft+Technik"

Weitere Artikel der Ausgabe 6/2011

Effect of CO2 laser treatment on cotton surface

Polylysine coated bacterial cellulose nanofibers as novel templates for bone-like apatite deposition

Synthesis and characterization of cellulose fibers grafted with hyperbranched poly(3-methyl-3-oxetanemethanol)

Polypyrrole (PPy) chemical synthesis with xylan in aqueous medium and production of highly conducting PPy/nanofibrillated cellulose films and coatings

Evolution of cellulose crystals during prehydrolysis and soda delignification of sugarcane lignocellulose

Preparation of the water-soluble chitosan-coated oxidized regenerated cellulose gauze