Kinetic aspects in the drying dissipative crack patterns of colloidal crystals

Kinetics of the dissipative structure formation in the course of drying the colloidal crystals of silica spheres (103 nm in diameter) in aqueous deionized suspension on a rinsed cover glass has been studied by the close-up video observation. The patterns of the broad ring of the hill accumulated with the spheres coexisted with the many spoke-like cracks. The characteristic convection flow of the spheres and the interactions between the spheres and substrate were important for the pattern formation. Cracks formed suddenly in the course of drying along the outside edge first, then toward the center, and stopped around the middle point between the outside edges and the frontier of suspension area. The further growth of the cracks took place at the adjacent place of the previous crack side by side and cooperatively. After the fast formation of these cooperative spoke-like cracks was completed, then all the crack lines further developed very slowly and simultaneously toward the center with the similar rate as that of the movement of the drying frontier of the suspension area toward center. Rates of the fast and slow modes of crack formation were 6.2 mm/s and 0.0098 mm/s, respectively, at the sphere concentration of 0.033 in volume fraction.