LaAlO3 doped (Mg0.95Zn0.05)TiO3–CaTiO3 ceramic system with ultra-high-Q and temperature-stable characterization
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 8/2015
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The microstructures and microwave dielectric properties of 1.0 mol% LaAlO3 doped 0.95(Mg0.95Zn0.05)TiO3–0.05CaTiO3 ceramics prepared by the conventional solid-state reaction route were investigated, for achieving a material with a high quality factor and nearly zero temperature coefficient of resonant frequency (τ
f
). The crystalline phases and the microstructures of the ceramics were characterized by means of X-ray diffraction and scanning electron microscopy. By Zn substitution, the Q × f values of the ceramics were significantly promoted. Moreover, the sintering temperature of the ceramic can be lowered to 1200 °C due to the effect of LaAlO3 as well as ZnO. The optimized microwave dielectric properties with εr ~ 22.5, Q × f value ~89,000 GHz and a τ
f
of ~−6.9 × 10−6/°C were achieved for 0.95(Mg0.95Zn0.05)TiO3–0.05CaTiO3 sintered at 1200 °C for 4 h.