Wettability of Mn_xSi_yO_z by Liquid Zn-Al Alloys

The wettability of Mn_xSi_yO_z by liquid Zn-Al alloys was investigated to obtain basic information on the coating properties of high-strength steels with surface oxides in the hot-dip galvanizing process. In this study, the contact angles of liquid Zn-Al alloys (Al concentrations were 0.12 and 0.23 wt pct) on four different Mn_xSi_yO_z oxides, namely MnO, MnSiO₃, Mn₂SiO₄, and SiO₂, were measured with the dispensed drop method. The contact angle did not change across time. With an increasing Al concentration, the contact angle was slightly decreased for MnO and Mn₂SiO₄, but there was no change for MnSiO₃ and SiO₂. With an increasing SiO₂ content, the contact angle gradually increased by 54 wt pct to form MnSiO₃, and for pure SiO₂ substrate, the contact angle decreased again. Consequently, the MnSiO₃ substrate showed the worst wettability among the four tested oxide substrates.