Structural investigation of bismuth borate glass ceramics containing gadolinium ions by X-ray diffraction and FTIR spectroscopy
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 4/2009
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
X-ray diffraction and FTIR spectroscopy measurements have been employed to investigate the xGd2O3 · (100 − x)[2Bi2O3 · B2O3] glass ceramics system, with 0 ≤ x ≤ 20 mol%. Heat treatment of glass samples at 625 °C for 24 h led to the formation of two crystalline phases. One crystalline phase is for the sample without gadolinium ions which belongs to the cubic system and another one is for the sample containing 20 mol% Gd2O3 which is orthorhombic with two unit cell parameters very close to each other. Between x = 0 mol% and x = 20 mol% there is a mixture of these crystalline phases. FTIR spectroscopy data suggest that the gadolinium ions play the network modifier role in the studied glasses. These data show that the glass structure consists of the BiO3, BiO6, BO3, and BO4 structural units, and the conversion among these units mainly depends on the Gd2O3 content.