Low temperature synthesis of Li₅La₃Nb₂O₁₂ with cubic garnet-type structure by sol–gel process

A cubic Li₅La₃Nb₂O₁₂ phase with a garnet framework was synthesized by the sol–gel process, in which lithium hydroxide, niobium oxide and acetic lanthanum were used as starting materials, while water was used as solvent. Pure garnet-like Li₅La₃Nb₂O₁₂ powders were obtained after heating the gel precursor at 700 °C for 6 h with 10 % excess lithium salt. The calcination temperature is nearly 250 °C lower than that by the solid state reaction. The phase transforms from cubic to tetragonal symmetry with loss of lithium at 717 °C, but the garnet framework remains stable to above 900 °C. A pellet annealed at 900 °C for 6 h had a room-temperature Li⁺-ion conductivity σ_Li (22 °C) = 1.0 × 10⁻⁵ S cm⁻¹, a little higher than that attained by solid-state synthesis. The Li₅La₃Nb₂O₁₂ compound was chemically stable against two commonly used cathode materials, LiMn₂O₄ and LiCoO₂, up to 900 °C and against metallic lithium.