The Role of Retained Austenite on the Mechanical Properties of a Low Carbon 3Mn-1.5Ni Steel

The present studies focus on the correlation between retained austenite characteristics and the cryogenic temperature Charpy impact toughness, strength, and plasticity. The steels with different volume fractions and stabilities of retained austenite were prepared by quenching followed by intercritical heat treatment, and the microstructure was characterized using scanning electron microscope, electron back-scattered diffraction, and X-ray diffraction. The grain size, dislocation density, crack initiation energy, and crack propagation energy were quantified. It has been demonstrated that the volume fraction of retained austenite plays a significant role in the reduction of the measured yield strength and the effect of tempered martensite/ferrite matrix on cryogenic temperature impact toughness can be assumed to be similar due to the similar grain size, dislocation density and element content in solution for different heat treatments. It was found that the stability of retained austenite plays a determining role in the increase of cryogenic temperature impact toughness. Furthermore, the dependence of the crack propagation energy on retained austenite is much greater than that of the crack initiation energy. Generally, an excellent UTS × TEL does not produce good cryogenic temperature impact toughness.