Thermal properties and crystallization of PbO–MoO₃–P₂O₅ glasses

Thermal properties and crystallization of glasses from PbO–MoO₃–P₂O₅ ternary system were studied in three compositional series (100 − x)[0.5PbO–0.5P₂O₅]–xMoO₃ (A), 50PbO–yMoO₃–(50 − y)P₂O₅ (B), and (50 − z)PbO–zMoO₃–50P₂O₅ (C). Glass transition temperature, crystallization temperature, coefficient of thermal expansion, and dilatation softening temperature of the studied glasses were determined by differential thermal analysis and dilatometry. Crystallization products of annealed glass samples were investigated by X-ray diffraction and Raman spectroscopy. X-ray diffraction analysis of crystallized glasses revealed the formation of PbP₂O₆, Pb₃P₄O₁₃, and PbMoO₄ in the samples of the B series. In the series A and C in the samples with a high MoO₃ content, crystalline compounds of Pb(MoO₂)₂(PO₄)₂ and (MoO₂)(PO₃)₂, respectively, were identified. Raman spectra of crystalline samples confirmed the results of X-ray diffraction measurements and provided also information on thermal stability of glasses and formation of glass-crystalline phases in the studied glass series.