01.11.2014

Corrosion Behavior of Bare, Cr3C2-25%(NiCr), and Cr3C2-25%(NiCr)+0.4%CeO2-Coated Superni 600 Under Molten Salt at 900 °C

verfasst von: Deepa Mudgal, Sanjeet Kumar, Surendra Singh, Satya Prakash

Erschienen in: Journal of Materials Engineering and Performance | Ausgabe 11/2014

Einloggen, um Zugang zu erhalten
share
TEILEN

Abstract

Cr3C2-25(NiCr) and Cr3C2-25(NiCr)+0.4%CeO2 coatings were deposited on nickel-based superalloy Superni 600 by Detonation-gun technique. Studies were conducted on bare and coated alloys in molten salt environment (Na2SO4-25%NaCl) at 900 °C under cyclic condition. Characterization of the corrosion product was done using field emission scanning electron microscopy/energy dispersive spectroscopy and x-ray diffraction techniques. The bare Superni 600 shows penetration of corrosion beneath the metal layer thereby indicating internal oxidation. The coating of Cr3C2-25(NiCr) with 0.4%CeO2 leads to the formation of adherent scale.
Literatur
1.
Zurück zum Zitat M. Broström, “Aspects of Alkali Chloride Chemistry on Deposit Formation and High Temperature Corrosion in Biomass and Waste Fired Boilers,” Energy Technology and Thermal Process Chemistry, Umeå University, Umeå, Academic Dissertation 2010, ETPC Report 10-04, ISSN 1653-0551, ISBN 978-91-7459-009-8 M. Broström, “Aspects of Alkali Chloride Chemistry on Deposit Formation and High Temperature Corrosion in Biomass and Waste Fired Boilers,” Energy Technology and Thermal Process Chemistry, Umeå University, Umeå, Academic Dissertation 2010, ETPC Report 10-04, ISSN 1653-0551, ISBN 978-91-7459-009-8
2.
Zurück zum Zitat M. Montgomery, O. Biede, and O.H. Larsen, Experiences with Inconel 625 in Biomass and Waste Incineration Plants, Mater. Sci. Forum, 2006, 522–523, p 523–530 CrossRef M. Montgomery, O. Biede, and O.H. Larsen, Experiences with Inconel 625 in Biomass and Waste Incineration Plants, Mater. Sci. Forum, 2006, 522–523, p 523–530 CrossRef
3.
Zurück zum Zitat R.A. Rapp, Chemistry and Electrochemistry of Hot Corrosion of Metals, Mater. Sci. Eng., 1987, 87, p 319–327 CrossRef R.A. Rapp, Chemistry and Electrochemistry of Hot Corrosion of Metals, Mater. Sci. Eng., 1987, 87, p 319–327 CrossRef
4.
Zurück zum Zitat D.M. Johnson, D.P. Whittle, and J. Stringer, Mechanisms of Na 2SO 4-Induced Accelerated Oxidation, Corr. Sci., 1975, 15, p 739–751 D.M. Johnson, D.P. Whittle, and J. Stringer, Mechanisms of Na 2SO 4-Induced Accelerated Oxidation, Corr. Sci., 1975, 15, p 739–751
5.
Zurück zum Zitat L. Singh, V. Chawla, and J.S. Grewal, A Review on Detonation Gun Sprayed Coatings, JOMMCE, 2012, 11(3), p 243–256 L. Singh, V. Chawla, and J.S. Grewal, A Review on Detonation Gun Sprayed Coatings, JOMMCE, 2012, 11(3), p 243–256
6.
Zurück zum Zitat P. Fauchais and A. Vardelle, Thermal Sprayed coatings Used Against Corrosion and Corrosive Wear, Advanced Plasma Spray Application, Dr. Hamid Jazi, Ed., ISBN 978-953-51-0349-3, 2012, p 9 P. Fauchais and A. Vardelle, Thermal Sprayed coatings Used Against Corrosion and Corrosive Wear, Advanced Plasma Spray Application, Dr. Hamid Jazi, Ed., ISBN 978-953-51-0349-3, 2012, p 9
7.
Zurück zum Zitat N. Espallargas, J. Berget, J.M. Guilemany, A.V. Benedetti, and P.H. Suegama, Cr 3C 2-NiCr and WC-Ni Thermal Spray Coatings as Alternatives to Hard Chromium for Erosion-Corrosion Resistance, Surf. Coat. Technol., 2008, 202(8), p 1405–1417 CrossRef N. Espallargas, J. Berget, J.M. Guilemany, A.V. Benedetti, and P.H. Suegama, Cr 3C 2-NiCr and WC-Ni Thermal Spray Coatings as Alternatives to Hard Chromium for Erosion-Corrosion Resistance, Surf. Coat. Technol., 2008, 202(8), p 1405–1417 CrossRef
8.
Zurück zum Zitat Chang-Jiu Li and Akira Ohmori, The Lamellar Structure of Detonation Gun Sprayed Al 2O 3 Coating, Surf. Coat. Technol., 1996, 82, p 254–258 CrossRef Chang-Jiu Li and Akira Ohmori, The Lamellar Structure of Detonation Gun Sprayed Al 2O 3 Coating, Surf. Coat. Technol., 1996, 82, p 254–258 CrossRef
9.
Zurück zum Zitat J. Wang, L. Zhang, B. Sun, and Y. Zhou, Study of the Cr 3C 2-NiCr Detonation Spray Coating, Surf. Coat. Technol., 2000, 130, p 69–73 CrossRef J. Wang, L. Zhang, B. Sun, and Y. Zhou, Study of the Cr 3C 2-NiCr Detonation Spray Coating, Surf. Coat. Technol., 2000, 130, p 69–73 CrossRef
10.
Zurück zum Zitat M. Roy, A. Pauschitz, J. Wernisch, and F. Franek, The Influence of Temperature on the Wear of Cr 3C 2-25(NiCr) Coating-Comparison Between Nanocrystalline Grains and Conventional Grains, Wear, 2004, 257, p 799–811 CrossRef M. Roy, A. Pauschitz, J. Wernisch, and F. Franek, The Influence of Temperature on the Wear of Cr 3C 2-25(NiCr) Coating-Comparison Between Nanocrystalline Grains and Conventional Grains, Wear, 2004, 257, p 799–811 CrossRef
11.
Zurück zum Zitat H.S. Sidhu, B.S. Sidhu, and S. Prakash, Wear Characteristics of Cr 3C 2-NiCr and WC-Co Coatings Deposited by LPG Fueled HVOF, Tribol. Int., 2010, 43(5–6), p 887–890 CrossRef H.S. Sidhu, B.S. Sidhu, and S. Prakash, Wear Characteristics of Cr 3C 2-NiCr and WC-Co Coatings Deposited by LPG Fueled HVOF, Tribol. Int., 2010, 43(5–6), p 887–890 CrossRef
12.
Zurück zum Zitat J.K.N. Murthy and B. Venkataraman, Abrasive Wear Behaviour of WC-CoCr and Cr 3C 2-20(NiCr) Deposited by HVOF and Detonation Spray Processes, Surf. Coat. Technol., 2006, 200(8), p 265–2642 CrossRef J.K.N. Murthy and B. Venkataraman, Abrasive Wear Behaviour of WC-CoCr and Cr 3C 2-20(NiCr) Deposited by HVOF and Detonation Spray Processes, Surf. Coat. Technol., 2006, 200(8), p 265–2642 CrossRef
13.
Zurück zum Zitat X.M. Li, Y.Y. Yang, T.M. Shao, Y.S. Jin, and G. Berbezat, Impact Wear Performance of Cr 3C 2-NiCr Coatings by Plasma and HVOF Spraying, Wear, 1997, 202, p 208–214 CrossRef X.M. Li, Y.Y. Yang, T.M. Shao, Y.S. Jin, and G. Berbezat, Impact Wear Performance of Cr 3C 2-NiCr Coatings by Plasma and HVOF Spraying, Wear, 1997, 202, p 208–214 CrossRef
14.
Zurück zum Zitat S. Wirojanupatump, P.H. Shipway, and D.G. McCartney, The Influence of HVOF Powder Feedstock Characteristics on the Abrasive Wear Behaviour of Cr x C y -NiCr Coatings, Wear, 2001, 249, p 829–837 CrossRef S. Wirojanupatump, P.H. Shipway, and D.G. McCartney, The Influence of HVOF Powder Feedstock Characteristics on the Abrasive Wear Behaviour of Cr x C y -NiCr Coatings, Wear, 2001, 249, p 829–837 CrossRef
15.
Zurück zum Zitat S. Matthews, B. James, and M. Hyland, The Role of Microstructure in the Mechanism of High Velocity Erosion of Cr 3C 2-NiCr Thermal Spray Coatings: Part 1—As-sprayed Coatings, Surf. Coat. Technol., 2009, 203, p 1086–1093 CrossRef S. Matthews, B. James, and M. Hyland, The Role of Microstructure in the Mechanism of High Velocity Erosion of Cr 3C 2-NiCr Thermal Spray Coatings: Part 1—As-sprayed Coatings, Surf. Coat. Technol., 2009, 203, p 1086–1093 CrossRef
16.
Zurück zum Zitat S. Matthews, B. James, and M. Hyland, The Role of Microstructure in the Mechanism of High Velocity Erosion of Cr 3C 2-NiCr Thermal Spray Coatings: Part 2—Heat Treated Coatings, Surf. Coat. Technol., 2009, 203, p 1094–1100 CrossRef S. Matthews, B. James, and M. Hyland, The Role of Microstructure in the Mechanism of High Velocity Erosion of Cr 3C 2-NiCr Thermal Spray Coatings: Part 2—Heat Treated Coatings, Surf. Coat. Technol., 2009, 203, p 1094–1100 CrossRef
17.
Zurück zum Zitat S. Sharma, Abrasive Wear Study of Rare Earth Modified Coatings by Statistical Method, J. Therm. Spray Technol., 2012, 21, p 773–781 CrossRef S. Sharma, Abrasive Wear Study of Rare Earth Modified Coatings by Statistical Method, J. Therm. Spray Technol., 2012, 21, p 773–781 CrossRef
18.
Zurück zum Zitat L. Zhu, X. Peng, J. Yan, and F. Wang, Oxidation of a Novel Chromium Coating with CeO 2 Dispersions, Oxid. Met., 2004, 62(5/6), p 411–426 CrossRef L. Zhu, X. Peng, J. Yan, and F. Wang, Oxidation of a Novel Chromium Coating with CeO 2 Dispersions, Oxid. Met., 2004, 62(5/6), p 411–426 CrossRef
19.
Zurück zum Zitat B. Yin, G. Liu, H. Zhou, J. Chen, and F. Yan, Sliding Wear Behaviour of HVOF-Sprayed Cr 3C 2-NiCr/CeO 2 Composite Coatings at Elevated Temperature up to 800 °C, Tribol. Lett., 2010, 37, p 463–475 CrossRef B. Yin, G. Liu, H. Zhou, J. Chen, and F. Yan, Sliding Wear Behaviour of HVOF-Sprayed Cr 3C 2-NiCr/CeO 2 Composite Coatings at Elevated Temperature up to 800 °C, Tribol. Lett., 2010, 37, p 463–475 CrossRef
20.
Zurück zum Zitat K.L. Wang, Q.B. Zhang, M.L. Sun, X.G. Wei, and Y.M. Zhu, Rare Earth Elements Modification of Laser-Clad Nickel-Based Alloy Coatings, Appl. Surf. Sci., 2000, 174, p 191–200 CrossRef K.L. Wang, Q.B. Zhang, M.L. Sun, X.G. Wei, and Y.M. Zhu, Rare Earth Elements Modification of Laser-Clad Nickel-Based Alloy Coatings, Appl. Surf. Sci., 2000, 174, p 191–200 CrossRef
21.
Zurück zum Zitat J. Yan, X. Peng, and F. Wang, Oxidation of a Novel CeO 2-Dispersion-Strengthened Chromium Coating in Simulated Coal-Combustion Gases, Mater. Sci. Eng. A, 2006, 2006(426), p 266–273 CrossRef J. Yan, X. Peng, and F. Wang, Oxidation of a Novel CeO 2-Dispersion-Strengthened Chromium Coating in Simulated Coal-Combustion Gases, Mater. Sci. Eng. A, 2006, 2006(426), p 266–273 CrossRef
22.
Zurück zum Zitat J.C. Colson, H. Buscail, G. Bonnet, M. Lachkar, and J.P. Larpin, The Effect of Deposited Rare Earth Oxide Films on High Temperature Corrosion Behaviour of Different Metals and Alloys, Solid State Phenom., 1995, 41, p 165–176 CrossRef J.C. Colson, H. Buscail, G. Bonnet, M. Lachkar, and J.P. Larpin, The Effect of Deposited Rare Earth Oxide Films on High Temperature Corrosion Behaviour of Different Metals and Alloys, Solid State Phenom., 1995, 41, p 165–176 CrossRef
23.
Zurück zum Zitat P.Y. Hou and J. Stringer, The Effect of Reactive Element Additions on the Selective Oxidation, Growth and Adhesion of Chromia Scale, Mater. Sci. Eng. A, 1995, 202, p 1–10 CrossRef P.Y. Hou and J. Stringer, The Effect of Reactive Element Additions on the Selective Oxidation, Growth and Adhesion of Chromia Scale, Mater. Sci. Eng. A, 1995, 202, p 1–10 CrossRef
24.
Zurück zum Zitat D.P. Whittle and J. Stringer, Improvements in High Oxidation Resistance by Addition of Reactive Elements or Oxide Dispersions, Philos. Trans. R. Lond., 1980, A295, p 309–329 CrossRef D.P. Whittle and J. Stringer, Improvements in High Oxidation Resistance by Addition of Reactive Elements or Oxide Dispersions, Philos. Trans. R. Lond., 1980, A295, p 309–329 CrossRef
25.
Zurück zum Zitat M.F. Pillis, E.G. de Araujo, and L.V. Ramanathan, Effect of Addition of Rare Earth Oxide Concentrates on Oxidation Behaviour of AISI, 304L Stainless Steel, TMS Lett., 2004, 1(3), p 57–58 M.F. Pillis, E.G. de Araujo, and L.V. Ramanathan, Effect of Addition of Rare Earth Oxide Concentrates on Oxidation Behaviour of AISI, 304L Stainless Steel, TMS Lett., 2004, 1(3), p 57–58
26.
Zurück zum Zitat J. Yan, X. Peng, and F. Wang, Oxidation of a Novel CeO 2-Dispersion-Strengthened Chromium Coating in Simulated Coal-Combustion Gases, Mater. Sci. Eng. A, 2006, 426, p 266–273 CrossRef J. Yan, X. Peng, and F. Wang, Oxidation of a Novel CeO 2-Dispersion-Strengthened Chromium Coating in Simulated Coal-Combustion Gases, Mater. Sci. Eng. A, 2006, 426, p 266–273 CrossRef
27.
Zurück zum Zitat K. Ogawa, K. Ito, T. Shoji, D.W. Seo, H. Tezuka, and H. Kato, Effects of Ce and Si Additions to CoNiCrAlY Bond Coat Materials on Oxidation Behaviour and Crack Propagation of Thermal Barrier Coatings, JTTEE ASM Int., 2006, 15, p 640–651 K. Ogawa, K. Ito, T. Shoji, D.W. Seo, H. Tezuka, and H. Kato, Effects of Ce and Si Additions to CoNiCrAlY Bond Coat Materials on Oxidation Behaviour and Crack Propagation of Thermal Barrier Coatings, JTTEE ASM Int., 2006, 15, p 640–651
28.
Zurück zum Zitat K.L. Wang, Q.B. Zhang, M.L. Sun, X.G. Wei, and Y.M. Zhu, Rare Earth Elements Modification of Laser-Clad Nickel-Based Alloys Coatings, Appl. Surf. Sci., 2001, 174, p 191–200 CrossRef K.L. Wang, Q.B. Zhang, M.L. Sun, X.G. Wei, and Y.M. Zhu, Rare Earth Elements Modification of Laser-Clad Nickel-Based Alloys Coatings, Appl. Surf. Sci., 2001, 174, p 191–200 CrossRef
29.
Zurück zum Zitat M.F. Pillis, E.G. de Araujo, and L.V. Ramanathan, Effect of Addition of Rare Earth Oxide Concentrate on Oxidation Resistance of AISI, 304L, Mater. Sci. Forum, 2006, 530–531, p 99–104 CrossRef M.F. Pillis, E.G. de Araujo, and L.V. Ramanathan, Effect of Addition of Rare Earth Oxide Concentrate on Oxidation Resistance of AISI, 304L, Mater. Sci. Forum, 2006, 530–531, p 99–104 CrossRef
30.
Zurück zum Zitat R.A. Mahesh, R. Jayagnthan, and S. Prakash, A Study on the Oxidation Behaviour of HVOF Sprayed NiCrAlY-0.4%CeO2 Coatings on Super Alloys at Elevated Temperature, Mater. Chem. Phys., 2010, 119, p 449–457 CrossRef R.A. Mahesh, R. Jayagnthan, and S. Prakash, A Study on the Oxidation Behaviour of HVOF Sprayed NiCrAlY-0.4%CeO2 Coatings on Super Alloys at Elevated Temperature, Mater. Chem. Phys., 2010, 119, p 449–457 CrossRef
31.
Zurück zum Zitat S. Kamal, R. Jayaganthan, and S. Prakash, Hot Corrosion Studies of Detonation-Gun-Sprayed NiCrAlY+0.4%CeO 2 Coated Superalloys in Molten Salt Environment, JMEPEG, 20, 2011, p 1068–1077 S. Kamal, R. Jayaganthan, and S. Prakash, Hot Corrosion Studies of Detonation-Gun-Sprayed NiCrAlY+0.4%CeO 2 Coated Superalloys in Molten Salt Environment, JMEPEG, 20, 2011, p 1068–1077
32.
Zurück zum Zitat H.S. Sidhu, B.S. Sidhu, and S. Prakash, Hot Corrosion Behavior of HVOF Sprayed Coatings on ASTM SA213-T11 Steel, J. Therm. Spray Technol., 2007, 16(3), p 349–354 CrossRef H.S. Sidhu, B.S. Sidhu, and S. Prakash, Hot Corrosion Behavior of HVOF Sprayed Coatings on ASTM SA213-T11 Steel, J. Therm. Spray Technol., 2007, 16(3), p 349–354 CrossRef
33.
Zurück zum Zitat S.S. Chatha, H.S. Sidhua, and B.S. Sidhu, High Temperature Hot Corrosion Behaviour of NiCr and Cr 3C 2-NiCr Coatings on T91 Boiler Steel in an Aggressive Environment at 750 °C, Surf. Coat. Technol., 2012, 206(19-20), p 3839–3850 CrossRef S.S. Chatha, H.S. Sidhua, and B.S. Sidhu, High Temperature Hot Corrosion Behaviour of NiCr and Cr 3C 2-NiCr Coatings on T91 Boiler Steel in an Aggressive Environment at 750 °C, Surf. Coat. Technol., 2012, 206(19-20), p 3839–3850 CrossRef
34.
Zurück zum Zitat T.S. Sidhu, S. Prakash, and R.D. Agrawal, Hot Corrosion Studies of HVOF Sprayed Cr 3C 2-NiCr and Ni-20Cr Coatings on Nickel-Based Superalloy at 900 °C, Surf. Coat. Technol., 2006, 201(3-4), p 792–800 CrossRef T.S. Sidhu, S. Prakash, and R.D. Agrawal, Hot Corrosion Studies of HVOF Sprayed Cr 3C 2-NiCr and Ni-20Cr Coatings on Nickel-Based Superalloy at 900 °C, Surf. Coat. Technol., 2006, 201(3-4), p 792–800 CrossRef
35.
Zurück zum Zitat S. Kamal, R. Jayaganthan, and S. Prakash, Evaluation of Cyclic Hot Corrosion Behaviour of Detonation Gun Sprayed Cr 3C 2-25%NiCr Coatings on Nickel- and Iron-Based Superalloys, Surf. Coat. Technol., 2009, 203, p 1004–1013 CrossRef S. Kamal, R. Jayaganthan, and S. Prakash, Evaluation of Cyclic Hot Corrosion Behaviour of Detonation Gun Sprayed Cr 3C 2-25%NiCr Coatings on Nickel- and Iron-Based Superalloys, Surf. Coat. Technol., 2009, 203, p 1004–1013 CrossRef
36.
Zurück zum Zitat R. Subhash Kamal, S. Jayaganthan, and P. Sanjay Kumar, Hot Corrosion Behavior of Detonation Gun Sprayed Cr 3C 2-NiCr Coatings on Ni and Fe-Based Superalloys in Na 2SO 4-60% V 2O 5 Environment at 900 °C, J. Alloys Compd., 2008, 463, p 358–372 CrossRef R. Subhash Kamal, S. Jayaganthan, and P. Sanjay Kumar, Hot Corrosion Behavior of Detonation Gun Sprayed Cr 3C 2-NiCr Coatings on Ni and Fe-Based Superalloys in Na 2SO 4-60% V 2O 5 Environment at 900 °C, J. Alloys Compd., 2008, 463, p 358–372 CrossRef
37.
Zurück zum Zitat M. Kaur, H. Singh, and S. Prakash, Role of Detonation Gun Spray Cr 3C 2-NiCr Coating in Improving High Temperature Corrosion Resistance of SAE-213-T22 and SAE-347H Steel in Presence of Na 2SO 4-82%Fe 2(SO 4) 3 Salt Deposits, Surf. Eng., 26(6), 2010, p 428–439 M. Kaur, H. Singh, and S. Prakash, Role of Detonation Gun Spray Cr 3C 2-NiCr Coating in Improving High Temperature Corrosion Resistance of SAE-213-T22 and SAE-347H Steel in Presence of Na 2SO 4-82%Fe 2(SO 4) 3 Salt Deposits, Surf. Eng., 26(6), 2010, p 428–439
38.
Zurück zum Zitat M. Kaur, H. Singh, and S. Prakash, High-Temperature Corrosion Studies of HVOF-Sprayed Cr 3C 2-NiCr Coating on SAE-347H Boiler Steel, J. Therm. Spray Technol., 2009, 18(4), p 619–632 CrossRef M. Kaur, H. Singh, and S. Prakash, High-Temperature Corrosion Studies of HVOF-Sprayed Cr 3C 2-NiCr Coating on SAE-347H Boiler Steel, J. Therm. Spray Technol., 2009, 18(4), p 619–632 CrossRef
39.
Zurück zum Zitat D. Deb, S. Ramakrishna Iyer, and V.M. Radhakrishnan, A Comparative Study of Oxidation and Hot Corrosion of a Cast Nickel Base Superalloy in Different Corrosive Environments, Mater. Lett., 1996, 29, p 19–23 CrossRef D. Deb, S. Ramakrishna Iyer, and V.M. Radhakrishnan, A Comparative Study of Oxidation and Hot Corrosion of a Cast Nickel Base Superalloy in Different Corrosive Environments, Mater. Lett., 1996, 29, p 19–23 CrossRef
40.
Zurück zum Zitat C.-J. Wang, Y.-C. Chang, and Y.-H. Su, The Hot Corrosion of Fe-Mn-Al-C Alloy with NaCl/Na 2SO 4 Coating Mixtures at 750 °C, Oxid. Met., 2003, 59(1/2), p 115–133 CrossRef C.-J. Wang, Y.-C. Chang, and Y.-H. Su, The Hot Corrosion of Fe-Mn-Al-C Alloy with NaCl/Na 2SO 4 Coating Mixtures at 750 °C, Oxid. Met., 2003, 59(1/2), p 115–133 CrossRef
41.
Zurück zum Zitat L. Zheng, Z. Maicang, and D. Jianxin, Hot Corrosion Behavior of Powder Metallurgy Rene95 Nickel-Based Superalloy in Molten NaCl–Na 2SO 4 Salts, Mater. Des., 2011, 32, p 1981–1989 CrossRef L. Zheng, Z. Maicang, and D. Jianxin, Hot Corrosion Behavior of Powder Metallurgy Rene95 Nickel-Based Superalloy in Molten NaCl–Na 2SO 4 Salts, Mater. Des., 2011, 32, p 1981–1989 CrossRef
42.
Zurück zum Zitat C.-C. Tsaur, J.C. Rock, C.-J. Wang, and S. Yung-Hua, The Hot Corrosion of 310 Stainless Steel with Pre-coated NaCl/Na 2SO 4 Mixtures at 750 °C, Mater. Chem. Phys., 2005, 89, p 445–453 CrossRef C.-C. Tsaur, J.C. Rock, C.-J. Wang, and S. Yung-Hua, The Hot Corrosion of 310 Stainless Steel with Pre-coated NaCl/Na 2SO 4 Mixtures at 750 °C, Mater. Chem. Phys., 2005, 89, p 445–453 CrossRef
43.
Zurück zum Zitat Y. Bourhis and C. St. John, Na 2SO 4- and NaCl-Induced Hot Corrosion of Six Nickel-Base Superalloys, Oxid. Met., 1975, 9(6), p 506–528 CrossRef Y. Bourhis and C. St. John, Na 2SO 4- and NaCl-Induced Hot Corrosion of Six Nickel-Base Superalloys, Oxid. Met., 1975, 9(6), p 506–528 CrossRef
44.
Zurück zum Zitat A. Rahman, R. Jayagahthan, R. Chandra, and R. Ambardar, High Temperature Degradation Behaviour Nanostructured Co-Al Coatings on Superalloy, Appl. Surf. Sci., 2013, 265, p 10–23 CrossRef A. Rahman, R. Jayagahthan, R. Chandra, and R. Ambardar, High Temperature Degradation Behaviour Nanostructured Co-Al Coatings on Superalloy, Appl. Surf. Sci., 2013, 265, p 10–23 CrossRef
45.
Zurück zum Zitat P. Viklund, A. Hjornhede, P. Henderson, A. Stalenheim, and R. Pettersson, Superheater Corrosion in a Waste-to-Energy Plant, Impacts of Fuel Quality on Power Production & Environment, Aug 29th, September 3rd 2010 Lapland, Finland P. Viklund, A. Hjornhede, P. Henderson, A. Stalenheim, and R. Pettersson, Superheater Corrosion in a Waste-to-Energy Plant, Impacts of Fuel Quality on Power Production & Environment, Aug 29th, September 3rd 2010 Lapland, Finland
46.
Zurück zum Zitat S. Karlsson, J. Pettersson, L.-G. Johansson, and J.-E. Sevensson, Alkali Induced High Temperature Corrosion of Stainless Steel: Influnce of NaCl, KCl and CaCl 2, Oxid. Met., 2012, 78, p 83–102 CrossRef S. Karlsson, J. Pettersson, L.-G. Johansson, and J.-E. Sevensson, Alkali Induced High Temperature Corrosion of Stainless Steel: Influnce of NaCl, KCl and CaCl 2, Oxid. Met., 2012, 78, p 83–102 CrossRef
47.
Zurück zum Zitat G.M. Ecer, R.B. Singh, and G.H. Meier, The Influence of Superficially Applied Oxide Powders on the High-Temperature Oxidation Behavior of Cr 2O 3-Forming Alloys, Oxid. Met., 1982, 18(1–2), p 55–87 CrossRef G.M. Ecer, R.B. Singh, and G.H. Meier, The Influence of Superficially Applied Oxide Powders on the High-Temperature Oxidation Behavior of Cr 2O 3-Forming Alloys, Oxid. Met., 1982, 18(1–2), p 55–87 CrossRef
48.
Zurück zum Zitat P. Kofstad, High Temperature Corrosion, Elsevier, London, 1988, p 558 P. Kofstad, High Temperature Corrosion, Elsevier, London, 1988, p 558
49.
Zurück zum Zitat D.R. Sigler, Oxidation Behavior of Fe-20Cr-5A1 Rare Earth Alloys in Air and Synthetic Exhaust Gas, Oxid. Met., 1991, 36, p 57–80 CrossRef D.R. Sigler, Oxidation Behavior of Fe-20Cr-5A1 Rare Earth Alloys in Air and Synthetic Exhaust Gas, Oxid. Met., 1991, 36, p 57–80 CrossRef
50.
Zurück zum Zitat H.P. Nielsen, F.J. Frandsen, and K. Dam-Johansen, Lab-Scale Investigations of High-Temperature Corrosion Phenomena in Straw-Fired Boilers, Energy Fuels, 1999, 13, p 1114–1121 CrossRef H.P. Nielsen, F.J. Frandsen, and K. Dam-Johansen, Lab-Scale Investigations of High-Temperature Corrosion Phenomena in Straw-Fired Boilers, Energy Fuels, 1999, 13, p 1114–1121 CrossRef
51.
Zurück zum Zitat G. Chen and H. Lou, Effect of Nanocrystallization on the Oxidation Behavior of a Ni-8Cr-3.5Al Alloy, Oxid. Met., 2000, 54(1/2), p 155–162 CrossRef G. Chen and H. Lou, Effect of Nanocrystallization on the Oxidation Behavior of a Ni-8Cr-3.5Al Alloy, Oxid. Met., 2000, 54(1/2), p 155–162 CrossRef
52.
Zurück zum Zitat C. Zhou, H. Xu, and S. Gong, Influence of Water Vapor on the Cyclic-Oxidation Behavior of a Low-Pressure Plasma-Sprayed NiCrAlY Coating, Oxid. Met., 2004, 62(3/4), p 195–206 CrossRef C. Zhou, H. Xu, and S. Gong, Influence of Water Vapor on the Cyclic-Oxidation Behavior of a Low-Pressure Plasma-Sprayed NiCrAlY Coating, Oxid. Met., 2004, 62(3/4), p 195–206 CrossRef
53.
Zurück zum Zitat S. Mingzeng, C. Lishan, Z. Yanjun, and X. Linlin, Effect of Cerium Addition on Oxidation Behaviour of 25Cr20Ni Alloy Under Low O Partial Pressure, J. Rare Earths, 2012, 30(2), p 164–169 CrossRef S. Mingzeng, C. Lishan, Z. Yanjun, and X. Linlin, Effect of Cerium Addition on Oxidation Behaviour of 25Cr20Ni Alloy Under Low O Partial Pressure, J. Rare Earths, 2012, 30(2), p 164–169 CrossRef
54.
Zurück zum Zitat G. Sreedhar and V.S. Raja, Hot Corrosion of YSZ/Al 2O 3 Dispersed NiCrAlY Plasma-Sprayed Coatings in Na 2SO 4-10 wt.% NaCl Melt, Corros. Sci., 2010, 52, p 2592–2602 CrossRef G. Sreedhar and V.S. Raja, Hot Corrosion of YSZ/Al 2O 3 Dispersed NiCrAlY Plasma-Sprayed Coatings in Na 2SO 4-10 wt.% NaCl Melt, Corros. Sci., 2010, 52, p 2592–2602 CrossRef
55.
Zurück zum Zitat Y. Ding, “Effects of Elevated Temperature Exposure on the Microstructural Evolution of Ni(Cr)-Cr 3C 2 Coated 304 Stainless Steel,” Thesis submitted for the degree of Doctor of Philosophy at the University of Nottingham, 2009, p 191 Y. Ding, “Effects of Elevated Temperature Exposure on the Microstructural Evolution of Ni(Cr)-Cr 3C 2 Coated 304 Stainless Steel,” Thesis submitted for the degree of Doctor of Philosophy at the University of Nottingham, 2009, p 191
56.
Zurück zum Zitat K. Gibbard, A Thesis on High Temperature Synthesis of Cerium Sulphides and Kinetic Modelling, University of Florida, Gainesville, 2005 K. Gibbard, A Thesis on High Temperature Synthesis of Cerium Sulphides and Kinetic Modelling, University of Florida, Gainesville, 2005
57.
Zurück zum Zitat A. Amadeh, B. Pahlevani, and S. Heshmati-Manesh, Effects of Rare Earth Metal Addition on Surface Morphology and Corrosion Resistance of Hot-Dipped Zinc Coatings, Corros. Sci., 2002, 44, p 2321–2331 CrossRef A. Amadeh, B. Pahlevani, and S. Heshmati-Manesh, Effects of Rare Earth Metal Addition on Surface Morphology and Corrosion Resistance of Hot-Dipped Zinc Coatings, Corros. Sci., 2002, 44, p 2321–2331 CrossRef
58.
Zurück zum Zitat S. Sharma, Abrasive Wear Study of Rare Earth Modified Coatings by Statistical Method, J. Therm. Spray Technol., 2012, 21(5), p 773–781 CrossRef S. Sharma, Abrasive Wear Study of Rare Earth Modified Coatings by Statistical Method, J. Therm. Spray Technol., 2012, 21(5), p 773–781 CrossRef
59.
Zurück zum Zitat D. Zhang, Z. Luo, T. Yuan, and R. Wang, Effects of Rare earth Elements Erbium and Cerium on the Properties of Hardfacing Alloy, Adv. Mat. Res., 2011, 189–193, p 3488–3491 CrossRef D. Zhang, Z. Luo, T. Yuan, and R. Wang, Effects of Rare earth Elements Erbium and Cerium on the Properties of Hardfacing Alloy, Adv. Mat. Res., 2011, 189–193, p 3488–3491 CrossRef
60.
Zurück zum Zitat G.Y. Lai, Factors Affecting the Performances of Sprayed Chromium Carbide Coatings for Gas-Cooled Reactor Heat Exchangers, Thin Solids Films, 1979, 64, p 271–280 CrossRef G.Y. Lai, Factors Affecting the Performances of Sprayed Chromium Carbide Coatings for Gas-Cooled Reactor Heat Exchangers, Thin Solids Films, 1979, 64, p 271–280 CrossRef
61.
Zurück zum Zitat M. Detroye, F. Reniers, C. Buess-Herman, and J. Vereecken, Synthesis and Characterisation of Chromium Carbide, Appl. Surf. Sci., 1997, 120, p 85–93 CrossRef M. Detroye, F. Reniers, C. Buess-Herman, and J. Vereecken, Synthesis and Characterisation of Chromium Carbide, Appl. Surf. Sci., 1997, 120, p 85–93 CrossRef
62.
Zurück zum Zitat S. Matthews, B. James, and M. Hyland, The Effect of Heat Treatment on the Oxidation Mechanism of Blended Powder Cr 3C 2-NiCr Coatings, J. Therm. Spray Technol., 2010, 19(1–2), p 119–127 CrossRef S. Matthews, B. James, and M. Hyland, The Effect of Heat Treatment on the Oxidation Mechanism of Blended Powder Cr 3C 2-NiCr Coatings, J. Therm. Spray Technol., 2010, 19(1–2), p 119–127 CrossRef
63.
Zurück zum Zitat S. Kamal, R. Jayaghanthan, and S. Prakash, High Temperature Cyclic Oxidation and Hot Corrosion Behaviours of Superalloys at 900 °C, Bull. Mater. Sci., 2010, 33(3), p 299–306 CrossRef S. Kamal, R. Jayaghanthan, and S. Prakash, High Temperature Cyclic Oxidation and Hot Corrosion Behaviours of Superalloys at 900 °C, Bull. Mater. Sci., 2010, 33(3), p 299–306 CrossRef
64.
Zurück zum Zitat I. Gurrappa, Hot corrosion behaviour of CM 247 LC Alloy in Na 2SO 4 and NACl Environments, Oxid. Met., 1999, 51(5/6), p 353–382 CrossRef I. Gurrappa, Hot corrosion behaviour of CM 247 LC Alloy in Na 2SO 4 and NACl Environments, Oxid. Met., 1999, 51(5/6), p 353–382 CrossRef
Metadaten
Titel
Corrosion Behavior of Bare, Cr3C2-25%(NiCr), and Cr3C2-25%(NiCr)+0.4%CeO2-Coated Superni 600 Under Molten Salt at 900 °C
verfasst von
Deepa Mudgal
Sanjeet Kumar
Surendra Singh
Satya Prakash
Publikationsdatum
01.11.2014
Verlag
Springer US
Erschienen in
Journal of Materials Engineering and Performance / Ausgabe 11/2014
Print ISSN: 1059-9495
Elektronische ISSN: 1544-1024
DOI
https://doi.org/10.1007/s11665-014-1177-3

Weitere Artikel der Ausgabe 11/2014

Journal of Materials Engineering and Performance 11/2014 Zur Ausgabe

Premium Partner

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.