Effect of TiC Particles Addition on Tribological Behavior of Ductile Iron

verfasst von: Yu Zhao, Wei Zhang, Yingdong Qu, Shulin Dong, Rongde Li, Guoping Zhou, Ruirun Chen, Qi Wang, Wei Sun, Guanglong Li

Erschienen in: Tribology Letters | Ausgabe 1/2023

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

In order to improve the wear resistance of ductile iron, different contents of TiC particles are added into ductile iron used lost-foam casting and the tribological behavior of ductile iron is studied through a ball-on-disk sliding test. It is found that with the increase of TiC content, the pearlite content gradually increases, which is attributed to TiC promoting the heterogeneous nucleation of cementite and increasing cooling rate of the melt. The increase of pearlite content and the second-phase strengthening caused by TiC improve the hardness and tensile strength of ductile iron. Ductile iron has the best tensile strength (498 MPa) and hardness (168 HV1) with a TiC content of 1 wt.%. The wear resistance also increases with increasing TiC content. The wear volume is reduced from 0.14 to 0.03 mm³, and the main wear mechanism changes from adhesive wear to abrasive wear. The oxide layer produced by frictional heat on the worn surface and the hardened layer produced by strain hardening on the subsurface further improve the wear resistance. Therefore, the wear resistance of ductile iron is affected by the changes of microstructure before and after wear.

Graphical Abstract

Vorheriger Artikel Transition from Plastic Shearing to Fracture of Asperity Junctions: Role of a Critical Aspect Ratio

Nächster Artikel Control of Nanoscale Ripple Formation on Ionic Crystals by Atomic Force Microscopy

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Fontanari, V., Benedetti, M., Girardi, C., Giordanino, L.: Investigation of the lubricated wear behavior of ductile cast iron and quenched and tempered alloy steel for possible use in worm gearing. Wear 350–351, 68–73 (2016). https://doi.org/10.1016/j.wear.2016.01.006CrossRef

Zhang, H., Wu, Y.X., Li, Q.J., Hong, X.: Mechanical properties and rolling-sliding wear performance of dual phase austempered ductile iron as potential metro wheel material. Wear 406–407, 156–165 (2018). https://doi.org/10.1016/j.wear.2018.04.005CrossRef

Wang, B.X., Barber, G.C., Qiu, F., Zou, Q., Yang, H.Y.: A review: phase transformation and wear mechanisms of single-step and dual-step austempered ductile irons. J. Mater. Res. Technol. 9, 1054–1069 (2020). https://doi.org/10.1016/j.jmrt.2019.10.074CrossRef

Du, Y.Z., Gao, X.Q., Wang, X.L., Wang, X., Ge, Y.F., Jiang, B.L.: Tribological behavior of austempered ductile iron (ADI) obtained at different austempering temperatures. Wear 456–457, 203396 (2020). https://doi.org/10.1016/j.wear.2020.203396CrossRef

Souza Oliveira Pimentel, A., Luiz-Guesser, W., da Silva, W.J.R.C., Dolabella Portella, P., Woydt, M., Burbank, J.: Abrasive wear behavior of austempered ductile iron with niobium additions. Wear 440–441, 203065 (2019). https://doi.org/10.1016/j.wear.2019.203065CrossRef

Wang, B.X., Qiu, F., Barber, G.C., Pan, Y.M., Cui, W.W., Wang, R.: Microstructure, wear behavior and surface hardening of austempered ductile iron. J. Mater. Res. Technol. 9, 9838–9855 (2020). https://doi.org/10.1016/j.jmrt.2020.06.076CrossRef

Sckudlarek, W., Krmasha, M.N., Al-Rubaie, K.S., Preti, O., Milan, J.C.G., da Costa, C.E.: Effect of austempering temperature on microstructure and mechanical properties of ductile cast iron modified by niobium. J. Mater. Res. Technol. 12, 2414–2425 (2021). https://doi.org/10.1016/j.jmrt.2021.04.041CrossRef

Zheng, B.W., Dong, F.Y., Yuan, X.G., Zhang, Y., Huang, H.J., Zuo, X.J., Luo, L.S., Wang, L., Su, Y.Q., Wang, X., Shi, K.: Evaluation on tribological characteristics of (TiC+TiB)/Ti–6Al–4V composite in the range from 25 °C to 600 °C. Wear 450–451, 203256 (2020). https://doi.org/10.1016/j.wear.2020.203256CrossRef

Zheng, B.W., Dong, F.Y., Yuan, X.G., Huang, H.J., Zhang, Y., Zuo, X.J., Luo, L.S., Wang, L., Su, Y.Q., Li, W.D., Liaw, P.K., Wang, X.: Microstructure and tribological behavior of in situ synthesized (TiB+TiC)/Ti6Al4V (TiB/TiC=1/1) composites. Tribol. Int. 145, 106177 (2020). https://doi.org/10.1016/j.triboint.2020.106177CrossRef

10.

Zheng, K.L., Wei, X.S., Yan, B., Yan, P.F.: Ceramic waste SiC particle-reinforced Al matrix composite brake materials with a high friction coefficient. Wear 458–459, 203424 (2020). https://doi.org/10.1016/j.wear.2020.203424CrossRef

11.

Kalogeropoulou, S., Baud, L., Eustathopoulos, N.: Relationship between wettability and reactivity in Fe/SiC system. Acta Metal. Mater. 43, 907–912 (1995). https://doi.org/10.1016/0956-7151(94)00336-GCrossRef

12.

Qiu, F., Liu, T.S., Zhang, X., Chang, F., Shu, S.L., Yang, H.Y., Zhao, Q.L., Jiang, Q.C.: Application of nanoparticles in cast steel: An overview. China Foundry 17(2), 111–126 (2020). https://doi.org/10.1007/s41230-020-0037-zCrossRef

13.

Wang, B.X., Qiu, F., Cui, W.W., Jin, Y.P., Zhang, Y., Hu, Z.R., Barber, G.C.: Microstructure and tensile properties of graphite ductile iron improved by minor amount of dual-phased TiC–TiB₂ nanoparticles. Adv. Eng. Mater. 23, 2100246 (2021). https://doi.org/10.1002/adem.202100246CrossRef

14.

Zhang, H., Wang, W.X., Chang, F., Li, C.L., Shu, S.L., Wang, Z.F., Han, X., Zou, Q., Qiu, F., Jiang, Q.C.: Microstructure manipulation and strengthening mechanisms of 40Cr steel via trace TiC nanoparticles. Mater. Sci. Eng. A 822, 141693 (2021). https://doi.org/10.1016/j.msea.2021.141693CrossRef

15.

Chang, F., Zhang, H., Gao, Y.L., Shu, S.L., Qiu, F., Jiang, Q.C.: Microstructure evolution and mechanical property enhancement of high-Cr hot work die steel manipulated by trace amounts of nano-sized TiC. Mater. Sci. Eng. A 824, 141788 (2021). https://doi.org/10.1016/j.msea.2021.141788CrossRef

16.

Qiu, F., Zhang, H., Li, C.L., Wang, Z.F., Chang, F., Yang, H.Y., Li, C.D., Han, X., Jiang, Q.C.: Simultaneously enhanced strength and toughness of cast medium carbon steels matrix composites by trace nano-sized TiC particles. Mater. Sci. Eng. A 819, 141485 (2021). https://doi.org/10.1016/j.msea.2021.141485CrossRef

17.

Razavi, M., Rahimipour, M.R., Rajabi-Zamani, A.H.: Effect of nanocrystalline TiC powder addition on the hardness and wear resistance of cast iron. Mater. Sci. Eng. A 454–455, 144–147 (2007). https://doi.org/10.1016/j.msea.2006.11.035CrossRef

18.

Yi, D.Q., Yu, P.C., Hu, B., Liu, H.Q., Wang, B., Jiang, Y.: Preparation of nickel-coated titanium carbide particulates and their use in the production of reinforced iron matrix composites. Mater. Des. 52, 572–579 (2013). https://doi.org/10.1016/j.matdes.2013.05.097CrossRef

19.

Park, J.J., Hong, S.M., Park, E.K., Kim, K.Y., Lee, M.K., Rhee, C.K.: Microstructure and properties of SA 106B carbon steel after treatment of the melt with nano-sized TiC particles. Mater. Sci. Eng. A 613, 217–223 (2014). https://doi.org/10.1016/j.msea.2014.06.103CrossRef

20.

Hong, S.M., Park, E.K., Park, J.J., Lee, M.K., Gu Lee, J.: Effect of nano-sized TiC particle addition on microstructure and mechanical properties of SA-106B carbon steel. Mater. Sci. Eng. A 643, 37–46 (2015). https://doi.org/10.1016/j.msea.2015.07.026CrossRef

21.

Xiao, B.T., Fan, Z.T., Jiang, W.M., Liu, X.W., Long, W., Hu, Q.: Microstructure and mechanical properties of ductile cast iron in lost foam casting with vibration. J. Iron Steel Res. Int. 21, 1049–1054 (2014). https://doi.org/10.1016/S1006-706X(14)60182-5CrossRef

22.

Wang, B.X., Zhang, Y., Qiu, F., Hu, M., Cui, W.W., Hu, Z.R., Barber, G.C.: Simultaneously enhanced hardness and toughness of normalized graphite ductile irons by TiC-TiB₂ nanoparticles. Mater. Lett. 291, 129597 (2021). https://doi.org/10.1016/j.matlet.2021.129597CrossRef

23.

Xu, Z.M., Liang, G.F., Guan, Q.F., Jiang, Q.C.: TiC as heterogeneous nuclei of the (Fe, Mn)₃C and austenite intergrowth eutectic in austenite steel matrix wear resistant composite. Mater. Res. Bull. 39, 457–463 (2004). https://doi.org/10.1016/j.materresbull.2003.10.014CrossRef

24.

Lacaze, J., Sertucha, J., Åberg, L.M.: Microstructure of as-cast ferritic-pearlitic nodular cast irons. ISIJ Int. 56(9), 1606–1615 (2016). https://doi.org/10.2355/isijinternational.ISIJINT-2016-108CrossRef

25.

Zheng, B.C., Huang, Z.F., Xing, J.D., Wang, Y., Jian, Y.X., Xiao, Y.Y., Fan, X.: Three-body abrasive behavior of cementite–iron composite with different cementite volume fractions. Tribol. Lett. 62, 32 (2016). https://doi.org/10.1007/s11249-016-0683-xCrossRef

26.

Wang, Z.H., Zhang, X., Xu, F.L., Qian, K.C., Chen, K.M.: Effect of nodularity on mechanical properties and fracture of ferritic spheroidal graphite iron. China Foundry 16(6), 386–392 (2019). https://doi.org/10.1007/s41230-019-9080-zCrossRef

27.

Laine, J., Jalava, K., Vaara, J., Soivio, K., Frondelius, T., Orkas, J.: The mechanical properties of ductile iron at intermediate temperatures: The effect of silicon content and pearlite fraction. Int. J. Met. 15(2), 538–547 (2021). https://doi.org/10.1007/s40962-020-00473-8CrossRef

28.

Chen, C., Lv, B., Ma, H., Sun, D.Y., Zhang, F.C.: Wear behavior and the corresponding work hardening characteristics of Hadfield steel. Tribol. Int. 121, 389–399 (2018). https://doi.org/10.1016/j.triboint.2018.01.044CrossRef

29.

Meng, Y., Deng, J.X., Zhang, Y., Wang, S.J., Li, X.M., Yue, H.Z., Ge, D.L.: Tribological properties of textured surfaces fabricated on AISI 1045 steels by ultrasonic surface rolling under dry reciprocating sliding. Wear 460–461, 203488 (2020). https://doi.org/10.1016/j.wear.2020.203488CrossRef

30.

Trevisiol, C., Jourani, A., Bouvier, S.: Effect of hardness, microstructure, normal load and abrasive size on friction and on wear behaviour of 35NCD16 steel. Wear 388–389, 101–111 (2017). https://doi.org/10.1016/j.wear.2017.05.008CrossRef

31.

Schwingenschlögl, P., Niederhofer, P., Merklein, M.: Investigation on basic friction and wear mechanisms within hot stamping considering the influence of tool steel and hardness. Wear 426–427, 378–389 (2019). https://doi.org/10.1016/j.wear.2018.12.018CrossRef

32.

Garbar, I.I.: Gradation of oxidational wear of metals. Tribol. Int. 35, 749–755 (2002). https://doi.org/10.1016/S0301-679X(02)00032-4CrossRef

33.

Wang, Y.X., Yang, Y.J., Yang, H.J., Zhang, M., Ma, S.G., Qiao, J.W.: Microstructure and wear properties of nitrided AlCoCrFeNi high-entropy alloy. Mater. Chem. Phy. 210, 233–239 (2018). https://doi.org/10.1016/j.matchemphys.2017.05.029CrossRef

34.

Zambrano, O.A., Coronado, J.J., Rodríguez, S.A.: Tempering temperature effect on sliding wear at high temperatures in mottled cast iron. Tribol. Lett. 57, 19 (2015). https://doi.org/10.1007/s11249-014-0462-5CrossRef

35.

Zhang, Z.J., Zhang, B.S., Zhu, S.S., Yu, Y.Q., Wang, Z.Z., Zhang, X.C., Lu, B.: Microstructural characteristics and enhanced wear resistance of nanoscale Al₂O₃/13 wt%TiO₂-reinforced CoCrFeMnNi high entropy coatings. Surf. Coat. Technol. 412, 127019 (2021). https://doi.org/10.1016/j.surfcoat.2021.127019CrossRef

36.

Zhao, Z.Y., Zhang, L.Z., Bai, P.K., Du, W.B., Wang, S.W., Xu, X.Y., Dong, Q.N., Li, Y.X., Han, B.: Tribological behavior of in situ TiC/graphene/graphite/Ti6Al4V matrix composite through laser cladding. Acta Metall Sin (Engl Lett) 34, 1317–1330 (2021). https://doi.org/10.1007/s40195-021-01215-3CrossRef

37.

Wright, S.I., Nowell, M.M., Field, D.P.: A review of strain analysis using electron backscatter diffraction. Microsc. Microanal. 17, 316–329 (2011). https://doi.org/10.1017/S1431927611000055CrossRef

38.

Yan, X.C., Hu, J., Wang, L.Y., Chai, Z.S., Sun, W.H., Xu, W.: The coupled effect of thermal and mechanical stabilities of austenite on the wear resistance in a 0.2C–5Mn-1.6Si steel down to cryogenic temperatures. Wear 486–487, 204116 (2021). https://doi.org/10.1016/j.wear.2021.204116CrossRef

39.

Yan, X.C., Hu, J., Yu, H., Wang, C.C., Xu, W.: Unraveling the significant role of retained austenite on the dry sliding wear behavior of medium manganese steel. Wear 476, 203745 (2021). https://doi.org/10.1016/j.wear.2021.203745CrossRef

40.

Zamani, M., Ghasemi, H.M., Mizadeh, H.: Effect of variation of martensite with a constant carbon content on mechanical behavior and sliding wear of dual phase steels. Tribol. Lett. 70, 73 (2022). https://doi.org/10.1007/s11249-022-01616-0CrossRef

Titel: Effect of TiC Particles Addition on Tribological Behavior of Ductile Iron
verfasst von: Yu Zhao
Wei Zhang
Yingdong Qu
Shulin Dong
Rongde Li
Guoping Zhou
Ruirun Chen
Qi Wang
Wei Sun
Guanglong Li
Publikationsdatum: 01.03.2023
Verlag: Springer US
Erschienen in: Tribology Letters / Ausgabe 1/2023
Print ISSN: 1023-8883
Elektronische ISSN: 1573-2711
DOI: https://doi.org/10.1007/s11249-023-01701-y

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Graphical Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 1/2023

Influence of Defects in Graphene-Like Network of Diamond-Like Carbon on Silica Scale Adhesion

Transition from Plastic Shearing to Fracture of Asperity Junctions: Role of a Critical Aspect Ratio

Analytical Theory of Ice-Skating Friction with Flat Contact

Preparation of Nanofluid of Lanthanum Borate Nanosheets and Investigation of Its Tribological Properties and Tribomechanisms in Different Base Oils

Application of Tribological Artificial Neural Networks in Machine Elements

Influence of Surface Roughness on Press Fits

Premium Partner

Marktübersichten