Journal of Materials Engineering and Performance

Erschienen in:

19.11.2020

Evaluation of Nitriding, Nitrocarburizing, Organosilicon Interlayer, Diamond-Like Carbon Film and Duplex Plasma Treatment in the Wear and Corrosion Resistance of AISI 4340 Steel

verfasst von: Lucas de Almeida Pires de Campos, Larissa Solano de Almeida, Brunela Pereira da Silva, Miguel Rubira Danelon, Idalina Vieira Aoki, Marcos Dorigão Manfrinato, Luciana Sgarbi Rossino

Erschienen in: Journal of Materials Engineering and Performance | Ausgabe 12/2020

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Duplex treatments are performed to promote an additional property to a previous surface treatment to improve wear and corrosion resistance of the material, like the DLC film (diamond-like carbon) deposited on nitriding or nitrocarburizing surfaces on the AISI 4340 steel. The purpose of this work is to study the effect of the duplex treatment (nitriding + DLC and nitrocarburizing + DLC film deposition) on the wear and corrosion resistance of AISI 4340 steel. The nitrocarburizing treatments by plasma were performed with 80% N₂ + 17% H₂ + 3% CH₄ at 400, 450, 500, 525 and 550 °C for 5 h. The nitriding treatment by plasma at 450 °C was performed with 80% N₂ + 20% H₂ for 5 h. The interlayer deposition was performed using hexamethyldisiloxane as a precursor. The deposition of DLC film was performed by DC-PECVD method using 90% CH₄ + 10% Ar at 200 °C for 2 h. The duplex treatment was performed at the optimum temperature of the nitrocarburizing process. Micro-abrasive wear tests by fixed ball, and corrosion tests showed that all material treated presented lower wear volume and higher corrosion resistance than untreated material, but the duplex treatments provided greater wear and corrosion resistance than that observed on materials treated with only one type of treatment, showing that duplex treatment improves surface resistance of the AISI 4340 steel. The nitrocarburizing + DLC duplex treatment presented greater wear and corrosion resistance than nitriding + DLC duplex treatment, evidencing the great positive effect of carbon added to the treatment.

Vorheriger Artikel Effects of Ti Addition on Microstructure and Tribological Properties of In Situ Composite Carbide Coating WC-TiC/FeNi Fabricated by Plasma Transferred Arc Metallurgical Reaction

Nächster Artikel Effect of Heat Treatment on Microstructure and Performance of Nano-WC Particle-Strengthened Ni Composite Coatings by Electrobrush Plating

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

A.S.M. Cardoso, A.J. Abdalla, M.S.F. Lima, V.H.B. Scheid, and C.A.R.P. Baptista, Surface Heat Treatment of Steel 4340 and 300M Steel After Laser Welding, Rev. Bras. Apl. Vac., 2015, 34(1), p 5–13. https://doi.org/10.17563/rbav.v34i1.939CrossRef

R.M. Anazawa, A.J. Abdalla, T.M. Hashimoto, and M.S. Pereira, Comparative Study of Mechanical Properties of Steels 300M and 4340 Submitted to Treatments Isothermal and Intercritical, Rev. Bras. Apl. Vac., 2012, 31(1–2), p 32. https://doi.org/10.17563/rbav.v31i1-2.918CrossRef

A.S.M. Handbook, Properties and Selection: Irons, Steels, and High- Performance Alloys, v I, 10th ed., Metals Handbook, Ohio, 1990, p 2521p

H. Kovacı, Ö. Baran, A.F. Yetim, Y.B. Bozkurt, L. Kara, and A. Çelik, The Friction and Wear Performance of DLC Coatings Deposited on Plasma Nitrided AISI, 4140 Steel by Magnetron Sputtering Under Air and Vacuum Conditions, Surf. Coat. Technol., 2018, https://doi.org/10.1016/j.surfcoat.2018.05.084CrossRef

T. Morita, Y. Hirano, K. Asakura, T. Kumakiri, M. Ikenaga, and C. Kagaya, Effects of Plasma Carburizing and DLC Coating on Friction-Wear Characteristics, Mechanical Properties and Fatigue Strength of Stainless Steel, Mater. Sci. Eng. A, 2012, 558, p 349–355. https://doi.org/10.1016/j.msea.2012.08.011CrossRef

J. Robertson, Diamond-Like Amorphous Carbon, Mater. Sci. Eng. R, 2002, 37(4–6), p 129–138. https://doi.org/10.1016/s0927-796x(02)00005-0CrossRef

L.S. Almeida, A.R.M. Souza, L.H. Costa, E.C. Rangel, M.D. Manfrinato, and L.S. Rossino, Effect of Nitrogen in the Properties of Diamond-like Carbon (DLC) Coating on Ti₆Al₄V Substrate, Mater. Res. Express., 2020, 7(6), p 1–19. https://doi.org/10.1088/2053-1591/ab94fbCrossRef

V.S. Sundaram, Diamond like Carbon Film as a Protective Coating for High Strength Steel and Titanium Alloy, Surf. Coat. Technol., 2006, 201, p 2707–2711. https://doi.org/10.1016/j.surfcoat.2006.05.046CrossRef

R.L.O. Basso, R.J. Candal, C.A. Figueroa, D. Wisnivesky, and F. Alvarez, Influence of Microstructure on the Corrosion Behavior of Nitrocarburized AISI, H13 Tool Steel Obtained by Pulsed DC Plasma, Surf. Coat. Technol., 2009, 203, p 1293–1297. https://doi.org/10.1016/j.surfcoat.2008.10.006CrossRef

10.

T. Bell, Y. Sun, and A. Suhadi, Environmental and Technical Aspects of Plasma Nitrocarburizing, Vacuum, 2000, 59(1), p 14–23. https://doi.org/10.1016/S0042-207X(00)00250-5CrossRef

11.

F.A.P. Fernandes, S.C. Heck, C.A. Picone, and L.C. Casteletti, On the Wear and Corrosion of Plasma Nitrided AISI, H13, Surf. Coat. Technol., 2020, 381, p 125216. https://doi.org/10.1016/j.surfcoat.2019.125216CrossRef

12.

E. Boztepe, A.C. Alves, E. Ariza, L.A. Rocha, N. Cansever, and F. Toptan, A Comparative Investigation of the Corrosion and Tribocorrosion Behaviour of Nitrocarburized, Gas Nitrided, Fluidized-Bed Nitrided, and Plasma Nitrided Plastic Mould Steel, Surf. Coat. Technol., 2018, 334, p 116–123. https://doi.org/10.1016/j.surfcoat.2017.11.033CrossRef

13.

M.H. Sohi, M. Ebrahimi, A.H. Raouf, and F. Mahboubi, Effect of Plasma Nitrocarburizing Temperature on the Wear Behavior of AISI, 4140 Steel, Surf. Coat. Technol., 2010, 1, p S84–S89. https://doi.org/10.1016/j.surfcoat.2010.04.054CrossRef

14.

E.P. Ilic, A. Pardo, T. Suter, S. Mischler, P. Schmutz, and R.A. Hauert, Methodology for Characterizing the Electrochemical Stability of DLC Coated Interlayers and Interfaces, Surf. Coat. Technol., 2019, 1, p 402–413. https://doi.org/10.1016/j.surfcoat.2019.07.055CrossRef

15.

A. M. Oliveira. Estudo da influência da nitretação e nitrocementação por plasma sobre a redução da porosidade superficial em amostras de ferro puro sinterizados. 1998. Masters dissertation—Federal University of Santa Catarina, Graduate Program in Mechanical Engineering, Florianópolis, 1998. https://repositorio.ufsc.br/handle/123456789/158202. Accessed 18 Aug 2019

16.

J.O. Pereira Neto, R.O. da Silva, E.H. da Silva, J.A. Moreto, R.M. Bandeira, M.D. Manfrinato, and L.S. Rossino, Wear and Corrosion Study of Plasma Nitriding F53 Super Duplex Stainless Steel, Mater. Res., 2016, 19(6), p 1241–1252. https://doi.org/10.1590/1980-5373-mr-2015-0656CrossRef

17.

A. Celik, M. Karakan, A. Alsaran, and I. Efeoglu, The Investigation of Structural, Mechanical and Tribological Properties of Plasma Nitrocarburized AISI, 1020 Steel, Surf. Coat. Technol., 2005, 200, p 1926–1932. https://doi.org/10.1016/j.surfcoat.2005.08.027CrossRef

18.

E.L. Dalibón, L. Escalada, S. Simison, C. Forsich, D. Heim, and S.P. Brühl, Mechanical and Corrosion Behavior of Thick and Soft DLC Coatings, Surf. Coat. Technol., 2016, 1, p 101–109. https://doi.org/10.1016/j.surfcoat.2016.10.006CrossRef

19.

M.H. Ghasemi, B. Ghasemi, and H.R.M. Semnani, Wear Performance of DLC Coating on Plasma Nitride Astaloy Mo, Diam. Relat. Mater., 2019, 1, p 8–15. https://doi.org/10.1016/j.diamond.2019.01.016CrossRef

20.

E.L. Dalibón, M.A. Guitar, V. Trava-Airoldi, F. Mucklich, and S.P. Bruhl, Plasma Nitriding and DLC Coatings for Corrosion Protection of Precipitation Hardening Stainless Steel, Adv. Eng. Mater., 2015, 18(5), p 826–832. https://doi.org/10.1002/adem.201500411CrossRef

21.

D. Cruz, B.A. Souza, L.A.P. Campos, L.S. Almeida, J.A. Moreto, M.D. Manfrinato, N.C. Cruz, and L.S. Rossino, Projeto, construção e comissionamento de um reator para tratamento de nitretação iônica a plasma em aço P20, Rev. Bras. Apl. Vac., 2018, 37, p 102–113. https://doi.org/10.17563/rbav.v37i3.1107CrossRef

22.

L.S. Almeida, A.R.M. Souza, M.D. Manfrinato, and L.S. Rossino, Study of the Effect of Plasma Cleaning Treatment Parameters on Adhesion and Wear Resistance of Ti₆Al₄V DLC Films, Rev. Bras. Apl. Vac., 2020, 39(1), p 45–55. https://doi.org/10.17563/rbav.v39i1.1161CrossRef

23.

C. Casiraghi, A.C. Ferrari, and J. Robertson, Raman Spectroscopy of Hydrogenated Amorphous Carbons, Phys. Rev. B, 2005, 728, p 1–14. https://doi.org/10.1103/physrevb.72.085401CrossRef

24.

N. Vidakis, A. Antoniadis, and N. Bilalis, The VDI, 3198 Indentation Test Evaluation of a Reliable Qualitative Control for Layered Compounds, J. Mater. Process. Technol., 2003, 143–144, p 481–485. https://doi.org/10.1016/S0924-0136(03)00300-5CrossRef

25.

G. Capote, D.C. Lugo, J.M. Gutiérrez, G.C. Mastrapa, and V.J. Trava-Airoldi, Effect of Amorphous Silicon Interlayer on the Adherence of Amorphous Hydrogenated Carbon Coatings Deposited on Several Metallic Surfaces, Surf. Coat. Technol., 2018, 344, p 644–655. https://doi.org/10.1016/j.surfcoat.2018.03.093CrossRef

26.

K.L. Rutherford and I.M. Hutchings, A Micro-Abrasive Wear Test, with Particular Application to Coated Systems, Surf. Coat. Technol., 1996, 79, p 231–239. https://doi.org/10.1016/0257-8972(95)02461-1CrossRef

27.

S. Li and R.R. Manory, Surface Morphology and Compound Layer Pores of Plasma Nitrocarburized Low Carbon Steel, Metall. Mater. Trans. A., 1996, 1, p 135–143. https://doi.org/10.1007/BF02647754CrossRef

28.

B. Edenhofer, Physical and Metallurgical Aspects of Ionitriding—Part 1, Heat Treat. Met., 1974, 2, p 23–28

29.

Y. Sun and T. Bell, Plasma Surface Engineering of Low Alloy Steel, Mater. Sci. Eng. A, 1991, 140, p 419–434. https://doi.org/10.1016/0921-5093(91)90458-yCrossRef

30.

R.C.C. Rangel, N.C. Cruz, A. Milella, F. Fracassi, and E.C. Rangel, Barrier and Mechanical Properties of Carbon Steel Coated with SiOx/SiOxCyHz Gradual Films Prepared by PECVD, Surf. Coat. Technol., 2019, 1, p 124996. https://doi.org/10.1016/j.surfcoat.2019.124996CrossRef

31.

A. Moreno-Bárcenas, J.M. Alvarado-Orozco, J.M.G. Carmona, G.C. Mondragón-Rodríguez, J. González-Hernández, and A. García-García, Synergistic Effect of Plasma Nitriding and Bias Voltage on the Adhesion of Diamond-Like Carbon Coatings on M2 Steel by PECVD, Surf. Coat. Technol., 2019, 374, p 327–337. https://doi.org/10.1016/j.surfcoat.2019.06.014CrossRef

32.

R. D’Agostino, P. Favia, Y. Kawai, H. Ikegami, N. Sato, and F. Arefi-Khonsari, Advanced Plasma Technology, 1st ed., Wiley, Mörlenbach, 2008

33.

A. Grill and V. Patel, Characterization of Diamond-like Carbon by Infrared Spectroscopy, Appl. Phys. Lett., 1992, 8(2–5), p 2089–2091. https://doi.org/10.1063/1.107098CrossRef

34.

K.Y. Li and S.M. Hsu, A Quantitative Wear Measurement Method on Production Engine Parts: Effect of DLC Thin Films on Wear, Wear, 2019, 426–427, p 462–470. https://doi.org/10.1016/j.wear.2019.01.054CrossRef

35.

E.L. Dalibón, C. Lasorsa, A. Cabo, J. Cimetta, N. García, and S.P. Brühl, Tribological Properties of SiNx Films on PH Stainless Steel With and Without Nitriding as a Pre-treatment, Proc. Mater. Sci., 2012, 1, p 313–320. https://doi.org/10.1016/j.mspro.2012.06.042CrossRef

36.

E. Araújo Junior, R.M. Bandeira, M.D. Manfrinato, J.A. Moreto, R. Borges, S.S. Vales, P.A. Suzuki, and L.S. Rossino, Effect of Ionic Plasma Nitriding Process on the Corrosion and Micro-Abrasive Wear Behavior of AISI, 316L Austenitic and AISI, 470 Super-Ferritic Stainless Steels, J. Mater. Res. Technol., 2019, 1, p 2180–2191. https://doi.org/10.1016/j.jmrt.2019.02.006CrossRef

37.

H. Okubo, C. Tadokoro, T. Sumi, N. Tanaka, and S. Sasaki, Wear Acceleration Mechanism of Diamond-like Carbon (DLC) Films Lubricated with MoDTC Solution: Roles of Tribofilm Formation and Structural Transformation in Wear Acceleration of DLC Films Lubricated with MoDTC Solution, Tribol. Int., 2019, 133, p 271–287. https://doi.org/10.1016/j.triboint.2018.12.029CrossRef

38.

N. Yamauchi, A. Okamoto, H. Tukahara, K. Demizu, N. Ueda, T. Sone, and Y. Hirose, Friction and Wear of DLC Films on 304 Austenitic Stainless Steel in Corrosive Solutions, Surf. Coat. Technol., 2003, 174–175, p 465–469. https://doi.org/10.1016/S0257-8972(03)00406-7CrossRef

39.

C. Binder, Desenvolvimento de novos tipos de aços sinterizados auto lubrificantes a seco com elevada resistência mecânica Aliada a baixo coeficiente de atrito via moldagem de pós por Injeção. 2009. Doctoral Thesis - Federal University of Santa Catarina, Technological Center, Graduate Program in Science and Materials Engineering, Florianópolis, 2009. https://repositorio.ufsc.br/handle/123456789/92350. Accessed 13 Aug 2019

40.

R.C. Cozza, Study of the steady state of wear in micro-abrasive wear testes by rotative ball conducted on specimen of WC–Co P20 and M2 tool-steel, Matéria, 2018, https://doi.org/10.1590/S1517-707620170001.0322CrossRef

41.

H.S.M. Lopez, J.A. Moreto, M.D. Manfrinato, N.C. da Cruz, E.C. Rangel, and L.S. Rossino, Micro Abrasive Wear Behaviour Study of Carburization and Ion Plasma Nitriding of P20 Steel, Mat. Res., 2016, 19(3), p 686–694. https://doi.org/10.1590/1980-5373-MR-2015-0721CrossRef

42.

D.C. Wen, Microstructure and Corrosion Resistance of the Layers Formed on the Surface of Precipitation Hardenable Plastic Mold Steel by Plasma-Nitriding, Appl. Surf. Sci., 2009, 256(3), p 797–804. https://doi.org/10.1016/j.apsusc.2009.08.062CrossRef

43.

M.B. Karamiş, Wear Properties of Steel Plasma Nitrited at High Temperatures, Mater. Sci. Eng. A., 1993, 168(1), p 49–53. https://doi.org/10.1016/0921-5093(93)90269-kCrossRef

44.

G.A. Ranalli, A.S.N. Pallone, V.F. Pereira, R.G. Oliveira, and N.A. Mariano, Efeitos da nitretação por plasma com pós-oxidação e por banho de sal na resistência à corrosão de um aço ferramenta, RevistaMatéria, 2009, 14(2), p 814–823. https://doi.org/10.1590/S1517-70762009000200005CrossRef

45.

Z. Wang, C. Wang, Q. Wang, and J. Zhang, Electrochemical Corrosion Behaviors of a-C: H and a-C:NX: H Films, Appl. Surf. Sci., 2008, 254, p 3021–3025. https://doi.org/10.1016/j.apsusc.2007.10.088CrossRef

46.

A. Zeng, E. Liu, I.F. Annergren, S.N. Tan, S. Zhang, P. Hing, and J. Gao, EIS Capacitance Diagnosis of Nanoporosity Effect on the Corrosion Protection of DLC Films, Diam. Relat. Mater., 2002, 11, p 160–168. https://doi.org/10.1016/S0925-9635(01)00568-4CrossRef

47.

T. Maerten, R. Oltra, C. Jaoul, C. Le Niniven, P. Tristant, F. Meunier, and O. Jarry, Investigation of Diamond-like Carbon Coated Steel Corrosion: Enhancing the Optical Detection of Defects by a Controlled Electrochemical Activation, Surf. Coat. Technol., 2019, 363, p 344–351. https://doi.org/10.1016/j.surfcoat.2019.02.050CrossRef

48.

F.A. Delfín, S.P. Brühl, C. Forsich, and D. Heim, Carbon Based DLC Films: Influence of the Processing Parameters on the Structure and Properties, Revista Mater., 2018, 23, p 02. https://doi.org/10.1590/s1517-707620180002.0395CrossRef

49.

E.R. Petry, C.D. Boeira, F. Cemin, L.M. Leidens, L.T. Bim, D.G. Larrude, M.E.H. Maia da Costa, and C.A. Figueroa, Physicochemical Structure of SiCx: H to Improve DLC Adhesion on Steel, Surf. Eng., 2016, 32(10), p 779–785. https://doi.org/10.1080/02670844.2016.1159277CrossRef

50.

X.L. Peng and T.W. Clyne, Mechanical Stability of DLC Films on Metallic Substrates Part lI, - Interfacial Toughness, Debonding and Blistering, Thin Solid Films, 1998, 312, p 210–227. https://doi.org/10.1016/S0040-6090(97)00703-7CrossRef

51.

R. Braak, U. May, L. Onuseit, G. Repphun, M. Guenther, C. Schmid, and K. Durst, Accelerated Thermal Degradation of DLC-Coatings Via Growth Defects, Surf. Coat. Technol., 2018, 349, p 272–278. https://doi.org/10.1016/j.surfcoat.2018.05.063CrossRef

Titel: Evaluation of Nitriding, Nitrocarburizing, Organosilicon Interlayer, Diamond-Like Carbon Film and Duplex Plasma Treatment in the Wear and Corrosion Resistance of AISI 4340 Steel
verfasst von: Lucas de Almeida Pires de Campos
Larissa Solano de Almeida
Brunela Pereira da Silva
Miguel Rubira Danelon
Idalina Vieira Aoki
Marcos Dorigão Manfrinato
Luciana Sgarbi Rossino
Publikationsdatum: 19.11.2020
Verlag: Springer US
Erschienen in: Journal of Materials Engineering and Performance / Ausgabe 12/2020
Print ISSN: 1059-9495
Elektronische ISSN: 1544-1024
DOI: https://doi.org/10.1007/s11665-020-05277-9

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 12/2020

Synthesis and Characterization of CuO-NiO Nanocomposites for Electrochemical Supercapacitors

Effects of Cooling Parameter and Cryogenic Treatment on Microstructure and Fracture Toughness of AISI D2 Tool Steel

Experimental and Numerical Analysis on Dual Phase Steel (DP780) Sheet Forming Limit and Effect of Microstructure Evolution on Formability

Fabrication of High-Strength Zr-Based Composites by Spark Plasma Sintering

Recrystallization and Associated Twinning Evolution in Nickel-Based GH4141 Superalloy During Annealing

Microstructural and Mechanical Properties of Cu-Based Co-Mo-Reinforced Composites Produced by the Powder Metallurgy Method

Premium Partner

Marktübersichten