03.08.2020  Ausgabe 6/2020 Open Access
Experimental Study of Selfheating Ignition of LithiumIon Batteries During Storage: Effect of the Number of Cells
 Zeitschrift:
 Fire Technology > Ausgabe 6/2020
Wichtige Hinweise
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
1 Introduction
Lithiumion batteries (LIBs) are an important type of energy storage device with high specific energy, high power, and a long cycle life. Due to their advantages, LIBs have been widely used for commercial applications, such as laptops, mobile phones and electric vehicles. Because of the fast development of electric vehicle technology and the increasing demand for electric vehicles, the global market of LIBs is predicted to keep increasing to USD 93.1 billion by 2025 [
1].
However, LIBs are a new safety hazard because of their tendency to ignite and burn. Many fires resulting in economic losses and casualties have been reported [
2]. For example, two LIB fires happened in two Boeing 787 Dreamliners in January 2013 [
3]. In 2016, a series of LIB fires of Samsung mobile phones led to a recall of the Galaxy Note 7 around the world leading to a large falloff in sale.
Anzeige
Ignition of LIBs can be triggered by abuse conditions, including mechanical abuse (crushing, penetration), electrical abuse (external short circuit, overcharge), thermal abuse (overheating) or internal short circuit [
4]. All of these can initiate thermal runaway leading to fires. Unlike the first three abuse conditions, which require external factors, internal short circuit occurs inside LIB leading to spontaneous ignition. Since the Boeing 787 Dreamliner battery fires reported in 2013 [
5], spontaneous ignition of LIBs has been under closer scrutiny. The cause of spontaneous ignition has been thought to be internal short circuit only [
4–
6], until a recent study found that spontaneous ignition can occur without an internal short circuit but because of internal chemical reactions [
7]. Another possibility for spontaneous ignition of LIBs is by selfheating in open circuit condition, particularly when they are stacked forming a large pile in a warehouse or a cargo.
Selfheating is the tendency of certain materials to undergo spontaneous internal exothermic reactions causing an increase in their temperature [
8–
10]. Selfheating ignition has been studied in many organic materials, such as coal [
11], and shale [
12]. For large sizes of these materials, selfheating ignition can occur at low ambient temperatures [
8,
9]. This is because heat generation due to chemical reactions is proportional to sample volume, while heat losses are proportional to sample surface area. Therefore, when the sample size is relatively large, the heat generation rate can be higher than the heat dissipation rate, resulting in spontaneous ignition caused by selfheating [
9].
LIB ignition caused by various abuse conditions has been studied at both the small component scale and singlecell scale. By studying the chemical reactions using different combinations of components [
13,
14], the reactions of LIB thermal runaway have been identified [
15]. In the order of onset temperatures from low to high, these reactions include: SEI (solid electrolyte interphase) decomposition, the reaction of intercalated Lithium with electrolyte, positive active material decomposition and electrolyte decomposition. The kinetics of these reactions have been studied [
16] and employed in simulations of a single cell [
17]. Tobishima and Yamaki [
18] first experimentally studied selfheating ignition of a cylindrical LiCoO
_{2} LIB using oven experiments. After this, the effects of the state of charge (SOC) [
19], cathode materials [
20] and aging process [
21] on this onset temperature were investigated. In terms of spontaneous ignition of LIBs, the internal short circuit issue has been considered [
4–
6]. The formation and detection of the internal short circuit, and how it causes spontaneous ignition are three key research topics [
22–
24]. Once the internal short circuit happens, the temperature of LIBs increases rapidly because of joule heating. The temperature increase triggers the chemical reactions, leading to spontaneous ignition [
4]. Some works [
25–
27] have studied the critical selfignition temperature of a single cell using nondimensional analysis based on selfheating ignition theories. However, as only one cell was used in previous experiments [
13–
27], the number of cells and the consequent effects of heat transfer were neglected. The ignition of a LIB box has been numerically investigated by Hu et al. [
28]. Results show that insulating materials could decrease the critical temperature of selfheating ignition, because these materials reduce the heat dissipation of cells.
When multiple are cells stacked together during storage or transport, the critical selfheating ignition temperature could be lower than the temperature for one cell. We attempt to show the key symptom of selfheating, which is the ignition temperature decreases as the number of cells increases. This unique symptom proves the possibility of selfheating ignition of LIBs.
Anzeige
In order to verify if LIB fires can start by selfheating, isothermal oven experiments for benchscale samples are recommended [
8]. Other faster methods employed in LIB ignition investigations include differential scanning calorimetry (DSC) [
29], C80 microcalorimeter [
14], vent sizing package 2 (VSP2) adiabatic calorimeter [
29] and Copper Slug Battery Calorimeter (CSBC) [
30]. These methods are used to study component scale or singlebattery scale. Accelerating rate calorimetry (ARC) [
16] is another method to investigate selfheating for benchscale samples in an adiabatic environment, which does not consider heat transfer among samples. Additionally, considering the low onset temperature of selfheating and low reaction rate of selfheating reactions [
8,
31], the kinetics obtained by these methods do not correspond to the kinetics of slow selfheating ignition. In comparison, an oven is large enough to conduct benchscale samples and can provide constant temperature heating to study the heat transfer effects.
In the current study, for the first time in literature, the effect of the number of cells on the selfheating behaviour of LiCoO
_{2} LIBs at 30% SOC has been studied using oven experiments. The effective kinetics and effective thermal properties of LIBs are extracted based on selfheating ignition theory, and are used to predict selfheating ignition of LIBs at real sizes in storage and their dependence on the ambient temperature.
2 Selfheating Ignition Theory
The first theory to describe the selfheating phenomenon was put forward by Semenov [
8,
31]. This theory assumes a uniform temperature of the system, ignores the consumption of materials and assumes that heat generation is due to one global chemical reaction. These assumptions limit the wider utilization of Semenov theory because the temperature profile of most solid materials is not uniform. However, Semenov theory can effectively describe the selfheating problem of liquids.
In order to describe a more realistic temperature distribution of solids, FrankKamenetskii proposed a model that incorporated the heat conduction of Fourier’s law [
8,
31]. As the temperature variation of a substance itself can be calculated, FrankKamenetskii theory has been widely employed to investigate the characteristics of substance selfheating ignition [
12]. This theory also neglects fuel consumption and assumes that heat production is from a global chemical reaction based on Arrhenius law. According to these assumptions, the energy conservation of the FrankKamenetskii theory is shown in Eq. (
1):
where
\(k\) is the thermal conductivity of the fuel,
\(T\) is the temperature of the fuel at a location,
\(f\left( t \right)\) is the mass action law that depends on the concentration of reactants at any time,
\(\Delta H_{c}\) is the effective heat of reaction of the fuel,
\(E\) is the effective activation energy to describe the global reaction,
\(R\) is the universal gas constant,
\(\rho\) is the density of the fuel,
\(c\) is the heat capacity of the fuel and
\(t\) is time.
$$k\nabla^{2} T + f(t)\Delta H_{c} \exp \left( {\frac{  E}{RT}} \right) = \rho c\frac{\partial T}{\partial t}$$
(1)
FrankKamenetskii theory solves this transient heat conduction equation in steady state, as it assumes both the heat of reaction and effective activation energy of the material are large enough so that a steady state can be reached [
9,
12,
31]. In practical cases, this is a wellapproximated assumption as the temperature of the material is stable before ignition [
12]. As a result, the righthand side of the Eq. (
1) is equal to zero.
To solve Eq. (
1) at steady state, FrankKamenetskii defined a dimensionless heat generation number of
\(\delta\) [
8,
31], which is also known as the Damkohler number, shown in Eq. (
2):
where the
\(L\) is the characteristic length,
\(T_{\text{a}}\) is the ambient temperature,
\(f_{0}\) is the value of mass action law at initial time, which is a constant as the consumption of materials is ignored. As can be seen,
\(\delta\) increases as the characteristic length
\(L\) increases or as the ambient temperature
\(T_{\text{a}}\) increases.
$$\delta = \frac{{EL^{2} f_{0}\Delta H_{c} }}{{kRT_{a}^{2} }}e^{{  E/\left( {RT_{a} } \right)}}$$
(2)
FrankKamenetskii theory find that when
\(\delta\) is higher than a critical value
\(\delta_{c}\), thermal runaway occurs leading to ignition [
8,
31].
\(\delta_{c}\) is only related to the geometry of substance when the boundary condition
\(T = T_{a}\) can be satisfied. This boundary condition is easy to reach when convection is large. The values of
\(\delta_{c}\) can be found in literatures [
8,
31], for example, its value for an infinite slab is 0.878, and for a cube is 2.52. In this study, prismatic batteries have been used to study LIB selfheating ignition, the geometry of LIBs can be regarded as a cuboid. The
\(\delta_{c}\) value of a cuboid is not a constant but depends on the length of the three sides.
\(\delta_{c}\) can be calculated using the rectangular brick equation [
8], which is shown in Eq. (
3):
where a, b, c is the half length of three sides with relation of a < b, c.
$$\delta_{c} \left( {a,b,c} \right) = 0.84\left( {1 + 1/\left( {b/a} \right)^{2} + 1/\left( {c/a} \right)^{2} } \right)$$
(3)
At critical ignition condition, the dependence of the critical ambient temperature can be obtained by rearranging Eq. (
2) at critical ignition condition, and taking the logarithm, as shown in Eq. (
4):
where
\(T_{{{\text{a}},c}}\) is the minimum ambient temperature in which the ignition of the given sample size will occur.
$$\ln \left( {\frac{{\delta_{c} T_{a,c}^{2} }}{{L^{2} }}} \right) = \ln \left( {\frac{E}{R}\frac{{f\Delta H_{c} }}{k}} \right)  \frac{E}{R}\frac{1}{{T_{a,c} }}$$
(4)
By plotting the
\(\ln \left( {\frac{{\delta_{c} T_{{{\text{a}},c}}^{2} }}{{L^{2} }}} \right)\) against
\(\left( {\frac{1}{{T_{{{\text{a}},c}} }}} \right)\), a straightline correlation can be obtained if the onestep global Arrhenius reaction assumption is appropriate to apply to LIBs, which shows selfheating ignition can be modelled by FrankKamenetskii theory. The slope of the straight line is
\( \frac{E}{R}\), while the intercept corresponds to
\(\frac{E}{R}\cdot\frac{{f\Delta H_{c} }}{k}\). Thus, the effective kinetics and thermophysical parameters can be acquired.
3 Materials and Methods
3.1 LIB Samples
Sanyo UF103450P prismatic batteries with graphite anode and LiCoO
_{2} cathode were selected for experiments, due to their widespread use in consumer electronics and ease of purchase. The cell has a nominal voltage of 3.7 V and nominal capacity of 1880 mAh, with the dimension of 34 mm × 10 mm × 50 mm. Each cell has a burst disc as a safety vent on the positive side. When the internal pressure is higher than a threshold, this safety venting will release gases.
The state of charge (SOC) of 30% was selected for the experiments, as this is the maximum SOC allowed when batteries are shipped by air according to the Packing Instruction 965 (UM 3480) by IATA. Before the experiments, in order to measure the actual electrical capacity and ensure the same SOC, each cell was cycled three times at 0.2 C rate for 5 h at each charge or discharge process, with the final cycle to 30% SOC. After this, cells were rested for 5 h to avoid internal heat effects due to cycles.
3.2 Experimental Methods
The experimental setup employed to determine the critical minimum ambient temperature for selfheating ignition of LIB cells was based on the procedure in the British Standards EN 15188:2007. Figure
1 shows the overall experimental setup for studying selfheating ignition of cells with a different number of cells. Stacks of 1, 2, 3 and 4 cells were selected. Cells were stacked into a cuboid using wires around them to fix the shape, as this shape is easy to stack, to calculate
\(\delta_{c}\), and to ensure the internal conductive heat transfer. The physical dimensions of the different number of cells are shown in Table
1 to illustrate how they were stacked. According to Eq. (
3),
\(\delta_{c}\) and
\(\delta_{c} /L^{2}\) are calculated and shown in Table
1, which demonstrates that as the increase of the number of cells,
\(\delta_{c} /L^{2}\) decreases, and
\(\delta_{c}\) increases.
Bi numbers
\(\left( {Bi = \frac{{h_{c} L}}{k}} \right)\) are evaluated and shown in Table
1 to determine whether the lumped capacitance method can be used [
32], and justify which selfheating ignition theory should be chosen [
8]. The heat transfer coefficient
h
_{c} = 11 W/m
^{2} K is calculated from the experimental results (see Sect.
4.3). The effective conductivity of LIB
k = 1.08 W/m K was previously measured experimentally in [
33] for LiCoO
_{2}. The characteristic length
L is half the length of the smallest side. If
Bi < 0.1, the thermal resistance and the temperature gradient of cells are negligible, and therefore the lumped capacitance assumption can be employed [
8] and the Semenov theory should be chosen [
32]. Otherwise, when
Bi > 0.1, the lumped capacitance method is not satisfied [
8], and the FrankKamenetskii theory should be selected [
32].
Table 1
Physical Dimensions of Cells at Different Sizes, and Their
\(\delta_{c}\),
\(\delta_{c} /L^{2}\), Bi
Number

Width (a) (mm)

Length (b) (mm)

Height (c) (mm)

\(\delta_{c}\)

\(\delta_{c} /L^{2}\)

Bi


1

10

34

50

0.946

37,850.57

0.051

2

20

34

50

1.265

12,650.57

0.102

3

30

34

50

1.796

7983.91

0.154

4

40

34

50

1.835

6350.57

0.209

×
Cells were placed at the centre of a metal mesh cage in a thermostatically controlled 136 L oven, which has mechanically forced air circulation to prevent thermal stratification. Cells are strapped and fastened together using fine wires to fix the geometry and keep cells in contact with each other. This helps avoid the effect of thermal contact resistance due to swelling. Three thermocouples were employed to measure temperatures: one at the surface of the central cell (
T
_{c}), the second attached on the surface of one of the outmost cells (
T
_{s}), and the third used to monitor the ambient temperature (
T
_{a}). In order to monitor the voltage history during experiments, one of the central batteries was welded with nickel strip on both terminals, which were connected to the cycler using hightemperature resistant wires. The metal mesh cage was used to reduce the effects of airflow on results, and to prevent the fires and projectiles destroying the oven.
The minimum critical temperature,
\(T_{{{\text{a}},c}}\), is defined as the minimum ambient temperature that allows thermal runaway to happen causing ignition. When conducted an experiment, if cells failed to ignite, the experiment was repeated with fresh cells at a 10°C higher temperature. If cells reached ignition, the experiment was repeated with fresh cells at a 10°C lower temperature. The experiments were conducted until
\(T_{{{\text{a}},c}}\) was identified with the maximum error of ± 5°C for each number of cells. Then, the critical temperature experiments were repeated twice to decrease the error range. The total experiments carried out are summarised in Table
2. In total, 35 experiments corresponding to 158 h of oven run time were conducted.
Table 2
Total Number of Experiments Carried Out for the Different Number of Cells
Number of cells

1

2

3

4

Number of experiments

15

7

6

7

4 Results and Discussion
4.1 Selfheating Ignition Phenomenon
In general, in terms of LiCoO
_{2} cells at 30% SOC in our experiments, their selfheating ignition behaviours can be summarized into the following three stages: heating up, selfheating and thermal runaway. Taking a 1cell experiment at 173°C as an example, Fig.
2 presents its threestage selfheating ignition phenomenon and corresponding temperature profile. Table
3 also shows the criteria and observation of the three stages.
Table 3
Criteria and Observations of the 3 Stages in Selfheating Ignition
Stage

Criteria

Observation


I. Heating up

T
_{c} increases significantly above its initial temperature

(1) Slight swelling
(2) Fast
T
_{c} increase
(3) Slow Voltage decrease and rapid fluctuations (1st drop)
(4) Electrolyte leakage, if
T
_{a}≫
T
_{a,cr}

II. Selfheating

Crossover:
T
_{c}>
T
_{a}

(1) No obvious swelling
(2) Electrolyte leakage
(3) Colour of cathode gradually changes from white to yellow
(4) Crossover:
T
_{c} increases over
T
_{a}, followed by a slight drop, and a very slow increase
(5) 2nd voltage drops to zero and then recovers

III. Thermal runaway

T
_{c} increases sharply

(1) Rapid swelling in 2–3 s
(2) Plastic coating near cathode melting
(3) No further colour change at cathode
(4) Venting (
T
_{a}>
T
_{a,cr.}) and smoke. No flare, no fire and no sparks observed in any of our experiments
(5)
T
_{c} fast increase
(6) 3rd voltage drop to zero

×
Stage I:
Heating up
The first stage starts when a cell is heated significantly above its initial temperature once it has been placed into the oven. The cell temperature increased from the ambient temperature to oven temperature. In all experiments, cells initially began slightly swelling from their middle wall, due to thermal expansion. Once the temperature was higher than the onset temperature of SEI decomposition, this reaction started to generate gases, leading to the further swelling of cells For the experiments when
T
_{a}≫
T
_{a,cr}, electrolyte leakage was observed in this stage.
Stage II:
Selfheating
The second stage is characterised by the sample temperature exceeding the ambient temperature. As there is not a significant temperature increase in this stage, no obvious swelling was observed. Additionally, electrolyte leakage was often observed in this stage, in which the electrolyte began to leak out from the positive side, where there is a safety vent. This leakage leads to the gradual colour change of the cathode from white to yellow. The temperature increases over the ambient temperature due to selfheating, followed by a slight decrease because of the heat losses caused by the electrolyte leakage. After this, the cell temperature started to increase very slowly. When the electrolyte leakage was over, the cell appearance did not change further, but its temperature kept increasing. The heat accumulation in this stage maybe due to the SEI decomposition, reaction of intercalated Lithium with electrolyte, cathode positive material decomposition [
4,
15], or the chemical cross over between anode and cathode [
7].
Stage III:
Thermal runaway
As the cell temperature increased, thermal runaway happened leading to ignition. The cell rapidly swelled in 2–3 s, due to the fast internal gas generation. When the internal pressure exceeded the threshold, venting happened, as the stage III image shown in Fig.
2. Some smoke can be seen, but no flare, fire or sparks were observed during all experiments.
Moreover, for the first time in the literature, we find that selfheating ignition does not always cause venting. As shown in Fig.
3 of cell images after experiments, when the ambient temperature decreased to 169°C for a 1cell experiment, the cell selfheating ignition was also captured based on the temperature profile, but no venting happened. In all our experiments, the ignition without venting only happened in 1cell and 2cell experiments at their critical ignition temperature.
×
In order to fix the shape of stacks and keep cells in contact with each other, wires were used to fasten cells in all experiments. This method caused venting to happen prior to thermal runaway for 3cell and 4cell experiments, as wires limit the swelling of cells causing external pressure on the cell surface. Heat and mass losses due to the venting add an additional source of uncertainty to the experiments, but according to the critical temperatures we obtained, these losses do not affect results significantly. Without the fastening of cells using wires, selfheating ignition of 3cell and 4cell experiments did not happen even at 2cell critical ambient temperature. This is because the swelling of cell makes its surface curved, decreasing the physical contact areas between the cells reducing heat transfer, and therefore the cells do not behave as one body. Additionally, in terms of 1cell and 2cell experiments, because of small deformation and swelling in total, the wire fastening did not affect experiments in any visible way.
4.2 Temperature
Figure
4a, b shows an example of ignition and noignition of a 1 cell configuration to explain how to identify
\(T_{{{\text{a}},c}}\) using temperature data. Cells failed to be ignited at an ambient temperature of 162°C, but succeed to reach ignition at an ambient temperature of 169°C. In terms of the noignition cases, the cell temperature slightly exceeds the oven temperature firstly, and then it is cooled down to the oven temperature. This is because this oven temperature is the highest subcritical ambient temperature, however, heat generation due to chemical reaction in proportion to sample size is still slightly lower than heat losses proportion to sample surface. Regarding the ignition case, thermal runaway occurs at 106 min indicating the cell has ignited at the oven temperature of 169°C, which is the lowest supercritical ambient temperature. Therefore, the
\(T_{{{\text{a}},c}}\) of the 1 cell is 165.5 ± 3.5°C.
×
The experiments of the maximum ambient temperatures for noignition (left) and the experiments of the minimum ambient temperatures for ignition (right) among 1–4 cells are shown in Fig.
4. As the number of cells increases, the peak cell temperature and the minimum ambient temperature for ignition decreases. Additionally, according to the ignition cases in Fig.
4, the cell surface temperature in selfheating stage is equal to the ambient temperature,
\(T_{s} = T_{a}\), which satisfies the boundary condition of FrankKamenetskii theory.
The time to thermal runway, and the times of stage I and II are shown in Fig.
5. The time to thermal runaway equals to the sum of times of stage I and II. As the number of cells increases, the time of stage I increases linearly, while the time of stage II and the time to thermal runaway increase nonlinearly.
×
4.3 The Heat Transfer Coefficient
The effective heat transfer coefficient can be estimated using battery temperature data from the heating up stage in Fig.
4. According to Table
1, only 1 cell and 2 cells have Bi < 0.1. In these conditions, based on the lumped capacitance method [
32], we have:
\(\dot{Q} = Sh\left( {T_{a}  T_{s} } \right) = mc\left( {dT_{s} /dt} \right)\), the heat transfer coefficient is
\(h = mc\left( {dT_{s} /dt} \right)/S\left( {T_{a}  T_{s} } \right)\).
Figure
6 presents the plots of
dT
_{s}/
dt vs
T
_{a} −
T
_{s} for the critical ignition cases of 1 and 2 cells. The slopes correspond to
\(hS/mc\), which can be used to extract the heat transfer coefficient. The surface area
\(S\) is calculated using three side lengths, and the specific heat capacity
\(c\) is 990 J/kgK from previous experimental measurements of the same cell [
27], and the cell mass
\(m\) is 36.8 g. Therefore, the heat transfer coefficients of different number of cells can be calculated and are presented in Table
4. The final heat transfer coefficient we selected to calculate Bi number is 11 W/m
^{2} K.
Table 4
Heat Transfer Coefficient for the Different Number of Cells
Number of cells

1

2

Heat transfer coefficient (W/m
^{2} K)

11.83

10.89

×
4.4 Voltage
Figure
4 shows the voltage characteristics across the three stages, and different voltage histories for the noignition and ignition cases respectively. In terms of ignition cases, the voltages exhibit similar trends across the experiments. In the first stage, the voltage decreases as the cell temperature increases, because the high temperature can speed up the degradation of cells [
34]. There is always a fluctuation followed by the first voltage drop in this stage, which could be a signal of the start of an internal side reaction that is SEI decomposition as this has been regarded as the first side reaction during thermal runaway [
4]. Figure
7 gives the time to voltage fluctuation of experiments, and their corresponding cell temperatures at that time. As the ambient temperature increases, the time to voltage fluctuation decreases. This is because it takes a longer time to heat more cells at lower ambient temperature. However, no matter how many cells were used and what the ambient temperature was, the cell temperatures at the time of voltage fluctuation are all around 130°C, which is close to the onset temperature of SEI decomposition in previous studies [
4,
15].
×
In the second stage, the voltage suddenly decreases to zero right after the electrolyte leakage. When the electrolyte leakage finishes, the cell voltage can be detected again in the selfheating stage. Figure
8 gives the relationship between time to electrolyte leakage and time to the 2nd voltage drop of three 1cell experiments. Time to electrolyte leakage is defined as when we first observed the electrolyte leakage, and these values were always slightly smaller than time to the 2nd voltage drop.
×
After the 2nd voltage drop, the voltage decreases slowly. This may be caused by anode and cathode side reactions in hightemperatures, which could increase internal resistance by continuing to consume intercalated Lithium, generating further gases and impurities [
4].
In the third stage, when the temperature starts to increase rapidly, the voltage sharply decreases to zero again, which can be regarded as a signal that the cell has ignited.
4.5 Critical Ignition Temperature
Based on the ambient temperature data in Fig.
4, the critical temperatures of cell selfheating ignition are identified. The temperature values of 1, 2, 3 and 4 cells are 165.5 ± 3.5°C, 157 ± 2°C 155 ± 2°C and 153 ± 2°C, respectively.
In this work, a clear trend is shown, namely that the required ambient temperature for cell selfheating ignition decreases as the number of cells increases due to the heat transfer effects presented in the theory section. This trend should be satisfied not only for the prismatic cells used here, but also for any other shape of cells, such as cylindrical cells. This is because although the conductive contact area between cylindrical cells is smaller, heat transfer takes place among cells by conduction and radiation in the air gaps. The critical temperature for 4 cells is 153°C, which is still very high compared with ambient temperature. However, when cells are stacked in warehouses or shipped in cargoes, the number of cells is relatively large, and therefore, based on this critical ambient trend, cell selfheating ignition could happen and lead to fires.
4.6 Effective Kinetics and Thermal Properties
In order to quantify the effective kinetics and thermal properties, we assume that the boundary condition is
\(T_{s} = T_{a}\), which is a good assumption in this work as the temperature of the cell is approximately steady before ignition, as shown in Fig.
4. Using the critical ignition temperatures for 1–4 cells from Fig.
9, a figure of
\(ln\left( {{{\updelta }}_{c} T_{a}^{2} /L^{2} } \right)\) vs
\(1000/T_{a}\) is plotted. The best linear fit is calculated in the figure with an Rsquared value of 0.981. Figure
10 shows a typical FrankKamenetskii plot, which validates that the assumptions of FrankKamenetskii theory and onestep global Arrhenius reactions can be applied. The FrankKamenetskii plot also confirms that the ignition is caused by selfheating.
×
×
The slope of the straight line corresponds to
\( \frac{E}{R}\), while the yintercept is
\(ln\left( {\frac{E}{R}\cdot\frac{{f\Delta H_{c} }}{k}} \right).\) The effective conductivity
\(k\) of cells is highly related to cathode materials [
33]. In terms of LiCoO
_{2} cathode material, the effective conductivity
\(k\) is 1.08 W/mK [
33]. Based on this, the effective kinetics and thermal properties of the cell are extracted, as shown in Table
5. The errors are also shown in the table using the fits that give the highest and the lowest possible effective kinetics and thermal properties from the experimental data. These data we found in this work can contribute to predicting the cell selfheating ignition behaviour.
Table 5
Effective Activation Energy
\(E\) and
\(ln\left( {\frac{{\Delta H_{c} fE}}{Rk}} \right)\) of the Cell at 30% SOC Extracted from FrankKamenetskii Plot
\(k\) (W/m K)

\(E\) (kJ/mol) (− error, + error)

\(ln\left( {\frac{{\Delta H_{c} fE}}{Rk}} \right)\) (K
^{2}/m
^{2}) (− error, + error)

\(R^{2}\)


1.08 [
33]

230.78
(− 38.97, +83.40)

86.03
(− 16.72, +23.34)

0.981

5 Upscaling Study
In order to predict selfheating ignition of the cells used in this work at lower ambient temperatures, the properties in Table
5 are employed in the FrankKamenetskii theory to upscale the laboratory results. In these predictions, we use 1step effective kinetics of the cell. This method is widely used to predict selfheating phenomenon [
8,
12]. The 1step effective kinetics quantified from FrankKamenetskii theory includes the effect of multistep kinetics, and the prediction based on effective kinetics will need to be validated when largescale experiments become available. This upscaling result assumes cells are stacked into a cube so that the characteristic length equals to the ratio of volume to area and the
\(\delta_{c} = 2.52\).
Figure
11 shows the 1D upscaled results for the LiCoO
_{2} cell at 30% SOC. The critical temperature decreases significantly as the ratio of volume to area increases. For a 1000 Litre recycle bin (with a characteristic length of 0.5 m), a size commonly used for used LIBs collection, critical selfheating ignition temperature is 114°C (± 11°C), which is 50°C lower than that for a single cell. As LIBs in a recycle bin could be damaged and not pristine, the critical selfheating ignition temperature could be much smaller than this prediction.
×
According to results in Fig.
11, even this LIB type at 30% SOC can become hazardous at the highest credible ambient temperature of 40°C when its volume to area is higher than 52 m. But it is unlikely to happen when this LIB is free from manufacturing flaws or defects, because a cube with a side length of 52 m is far greater than realistic value even for large rack storage. However, other LIB types or this type but with manufacturing defects can become a hazard if their selfheating reactivity is higher. Additionally, the SOC in this study is only 30%, and the critical temperature of selfheating ignition may decrease with increasing SOC, as higher SOC potentially increases the reactivity of the LIB.
The upscaled results in Fig.
11 are only for the cells, not including the effects of packaging and boxes for storage, in which LIBs will be further insulated using separations and cushions, which could decrease the critical temperature of selfheating ignition [
28].
This study presents: (i) an experimental proof that LIB selfheating during storage is possible and likelihood increases with the size of the ensemble, (ii) a method to upscale laboratory experiments to study selfheating of any battery types, and (iii) evidence that the cell used in this work at 30% SOC will not selfheat to ignition even at large scales when it is free from manufacturing flaws.
6 Conclusions
In this study, the effect of the number of cells on the possibility of selfheating ignition of LIBs has been investigated using oven experiments. The Sanyo prismatic LiCoO
_{2} cells at 30% SOC were used in the experiments. Results show that selfheating ignition behaviour has three stages: heating up, selfheating, and thermal runaway. A previous study showed the critical ignition temperature for one 18650 LiCoO
_{2} cell was 155°C [
17]. However, this study has found that the critical ignition temperature decreases as number of cells increases, which implies selfheating ignition is possible for large LIB ensembles. As the number of cells increases from 1 to 4, the critical ambient temperature for selfheating ignition decreases from 165.5°C to 153°C. A FrankKamenetskii analysis using these critical temperatures shows a very good linear fit between thermal properties and inverse critical ambient temperature with an Rsquared value of 0.981, which confirms this is selfheating ignition. The effective kinetics
\(E\) is 230.78 kJ/mol and effective thermal properties
\(ln\left( {\frac{{\Delta H_{c} fE}}{Rk}} \right)\) is 86.03 K
^{2}/m
^{2}. These parameters are then used in the prediction of selfheating ignition of the cells during storage. Upscaling results show that this specific LIB type at 30% SOC is not particularly hazardous in terms of selfheating because the critical ambient temperature is high and safe enough. However, other LIB types with defects, higher SOC or being recycled could have a much larger reactivity. These LIBs could selfheat to ignition when they are stacked in a large enough ensemble during storage or transport. This work provides the first experimental study on selfheating ignition of LIBs in open circuit, contributing to understanding and predicting the onset of selfheating ignition of LIBs.
Acknowledgements
The authors would like to thank the support from China Scholarship Council (CSC) to Xuanze He and Zhenwen Hu. Many thanks to Dr Gregory Offer, Dr Yatish Patel, Yan Zhao and Eirik Christensen (Imperial College London) for their advice and help, and to Dr Jingwu Wang and Yang Peng (University of Science and Technology of China) for their help with the experiments.
Open AccessThis article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit
http://creativecommons.org/licenses/by/4.0/.
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.