Dielectric properties and high-temperature dielectric relaxation of tungsten-bronze structure ceramics Ba2GdFeNbTa3O15
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 1/2012
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Ba2GdFeNbTa3O15 was synthesized by a standard solid-state technique, which adopts a tetragonal filled tungsten bronze structure and exhibits paraelectric nature at room temperature. The dielectric temperature coefficient of Ba2GdFeNbTa3O15 at 1 MHz is 147 ppm °C
.
−1
AC impedance plots were used as tools to analyze the electrical behavior of the sample as a function of frequency at different temperatures. The conduction is a thermally activated process with activation energy ~1.30 eV. The frequency-dependent maxima in the imaginary part of impedance are found to obey an Arrhenius law with activation energy ~1.34 eV. Such a value of activation energy suggests the existence of a relaxation mechanism (a conductive process), which may be interpreted by an ion hopping between neighboring sites within the crystalline lattice.