Erschienen in:

Open Access 20.04.2019

A novel biocatalytic system obtained via immobilization of aminoacylase onto sol–gel derived ZrO₂·SiO₂ binary oxide material: physicochemical characteristic and catalytic activity study

verfasst von: Agnieszka Kołodziejczak-Radzimska, Filip Ciesielczyk, Teofil Jesionowski

Erschienen in: Adsorption | Ausgabe 4/2019

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Patentsuche

Aus

Abstract

Oxide material of a new type, ZrO₂·SiO₂ (raw and carbonyl-grafted), was used as support in the immobilization of aminoacylase from Aspergillus melleus. The ZrO₂·SiO₂ was synthesized via sol–gel method. The obtained material was additionally modified with glutaraldehyde. Various physicochemical analyses were used to confirm the effectiveness of the modification and immobilization processes, including Fourier transform infrared spectroscopy, laser Doppler velocimetry and low-temperature N₂ sorption. The immobilization process was performed within 3 h using different concentrations of enzyme solution (1, 3, 5 and 7 mg/mL), and the Bradford method was used to determine the quantity of immobilized enzyme. The resulting biocatalytic systems were then used as catalysts in the hydrolysis of different N-acetyl-dl-amino acids (leading to l-methionine, l-cysteine, l-serine and l-tryptophan). Based on this reaction the apparent and relative catalytic activities were determined. The highest activity of the immobilized enzyme was attained in the synthesis of l-methionine (the apparent activities of aminoacylase immobilized on raw and carbonyl-grafted ZrO₂·SiO₂ were 4112 and 4947 U/g, respectively). Furthermore, the effect of pH and temperature on catalytic activity, as well as the storage stability and reusability of the prepared biocatalytic systems were determined. Aminoacylase immobilized on carbonyl-grafted ZrO₂·SiO₂ retains 85% of its initial activity after 30 days of storage and 70% after five reaction cycles.

This article belongs to S.I. ISSHAC10, but it reach the press at the time the special issue was published.

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

1 Introduction

The fabrication of novel types of biocatalytic systems has gained great importance in recent years. Such systems are most commonly obtained via the immobilization of enzymes on various supports. There are several important aspects that should be considered when selecting an appropriate support for enzyme immobilization. First of all the support should be biocompatible and should have active functional groups on its surface (Wu et al. 2013). These groups should be stable in the reaction conditions, should exhibit low steric hindrance, and should enable combination with the amino acids groups present in the enzyme molecule. Additionally, the support should have good thermal, chemical and mechanical stability, and the surface should be hydrophilic. The support should also be insoluble in the reaction conditions. The most important factors are the ability to immobilize enzymes on the chosen material, and its price (Cowana and Fernandez-Lafuente 2011; Homaei et al. 2013). Inorganic hybrid materials exhibit most of the properties mentioned above, and offer higher thermal and mechanical stability than organic materials (Jesionowski et al. 2014). Moreover, these materials exhibit microbial resistance, because they do not serve as a matrix for the growth of bacteria and fungi, unlike more popular organic materials such as cellulose, polyamine and polydextrans. The inorganic materials do not change their structure in different pH and temperature conditions or in organic solvents, in contrast to organic materials and polymers. They have a higher modulus of elasticity than organic polymers. These materials have a highly hydrophilic surface, because of the hydroxyl groups present on it. That is why it is possible to modify their surface, promoting the creation of relatively stable interactions between enzymes and the support. Furthermore, many inorganic materials are characterized by high rigidity and porosity (Mateo et al. 2007).

The many different supports commonly used in the immobilization of enzymes include inorganic oxides such as SiO₂ (Kolodziejczak-Radzimska 2017; Jin et al. 2018), TiO₂ (Zivkovic et al. 2016; Haghighi et al. 2017) and ZrO₂ (Masuda et al. 2014), minerals such as bentonite (Cengiz et al. 2012) and halloysite (Zhai et al. 2010; Chao et al. 2013), and carbon materials (Mohiuddin et al. 2014; Wu et al. 2017; Das et al. 2018). These materials have been used in the immobilization of lipase (Cai et al. 2016; Zdarta et al. 2015; Kolodziejczak-Radzimska et al. 2018b; Heater et al. 2018), cysteine (Xiao et al. 2010; Noori et al. 2016), urease (Piccinini et al. 2017; Tak et al. 2017), α-amylase (Demkina et al. 2017), tyrosinase (Abdollahi et al. 2017), laccase (Pogorilyi et al. 2017) and other enzymes. As it can be seen a number of enzymes have been immobilized onto different materials. Additionally, this biocatalytic systems found their application in the treatment of industrial wastewaters. For instance, they were successfully applied for dye removal, degradation of pharmaceuticals, xenobiotics, and treatment of industrial effluents (Pylypchuk et al. 2018; Antecka et al. 2018).

Besides typical inorganic materials, interesting properties are offered by inorganic hybrids and composites and by oxide systems (Zdarta et al. 2018). These type of materials are synthesized from both organic and inorganic precursors. They are formulated to ensure the high stability of the resulting systems and good affinity to enzymes. Additionally, they contain numerous characteristic groups which show affinity to the chemical groups present in the protein structure (Ambrogio et al. 2011). The presence of functional groups enables the formation of covalent bonds with biomolecules, and ensures the good reusability and operational stability of the obtained biocatalytic systems.

Among the materials offering interesting properties are zirconia/silica oxide systems. These hybrid combine the properties of silica and zirconium oxide (Del Angel-Lopez et al. 2015), the most important of which are good stability, high strength, high fracture toughness, excellent wear resistance, high hardness and excellent chemical resistance (Jesionowski and Krysztafkiewicz 2001; Liang et al. 2009; Shibli et al. 2010; Klapiszewski et al. 2014). Due to its numerous advantages, the sol–gel process is commonly used for the production of nanostructured materials. This method makes it possible to obtain products that are homogeneous in terms of chemical composition, characterized by high purity and controlled physicochemical parameters. These types of materials are also useful in environmental applications, including the removal of various type of inorganic and organic impurities from water systems, via either adsorption or photocatalysis (Vaizogullar et al. 2015; Santos et al. 2014; Ciesielczyk et al. 2018).

In this study, for the first time, the ZrO₂·SiO₂ material was used as a support in the immobilization of aminoacylase from Aspergillus melleus. The simple, conventional adsorptive method has been used for enzyme immobilization. The adsorptive method as compared to other immobilization techniques is more simple and enables higher mobility of the enzyme, which in many cases results in a significant enzyme activity. The ZrO₂·SiO₂ was modified by glutaraldehyde to introduce carbonyl groups onto the surface. The products were analyzed by a number of techniques (including Fourier transform infrared spectroscopy, laser Doppler velocimetry and low-temperature N₂ sorption). The obtained biocatalytic systems were used as catalysts in the synthesis of selected amino acids (l-methionine, l-cysteine, l-serine and l-tryptophan).

2 Materials and methods

2.1 Materials

Solutions of tetraethyl orthosilicate (TEOS) and zirconium isopropoxide (TPZ), 25% ammonia solution (NH_3aq.) and ethyl alcohol (EtOH) were used in the synthesis of ZrO₂·SiO₂ as precursors, promotor of hydrolysis and solvent, respectively. Glutaraldehyde (GA) was used as a modifier. Aminoacylase from Aspergillus melleus (AAM), N-acetyl-l-methionine (AcMet), l-methionine (Met), N-acetyl-dl-serine, l-serine, N-acetyl-l-cysteine, l-cysteine, N-acetyl-dl-tryptophan, l-tryptophan, Bradford reagent, ninhydrin reagent, monobasic sodium phosphate (NaH₂PO₄) and dibasic sodium phosphate (Na₂HPO₄) were used in the immobilization process. All of the materials were purchased from Sigma-Aldrich^® (St Louis, MO).

2.2 Synthesis, modification and characterization of ZrO₂·SiO₂

The ZrO₂·SiO₂ oxide system was synthesized via a sol–gel method according to methodology presented in previously published article (Ciesielczyk et al. 2018). The product was obtained from organic precursors of silica (TEOS) and zirconia (TPZ). The molar ratio of the reagents was established as to obtain zirconia:silica ratio of 1:1. The 25% ammonia solution was used as promoter of hydrolysis and ethanol as a solvent. Resulting alcogel was gently dried at 105 °C within 12 h in order to slowly remove the solvent and enable the formation of well-developed porosity, so important in immobilization process. The material was thoroughly characterized with respect to parameters of the porous structure, type of surface functional groups (FTIR analysis) as well as electrokinetic stability (zeta potential measurements). Synthesized sample was furthermore modified with glutaraldehyde (5% solution). In this case the 1 g of ZrO₂·SiO₂ oxide material was stirred with the glutaraldehyde solution, and then filtered and dried (60 °C, 2 h). The resulting sample was labelled as ZrO₂·SiO₂_GA.

A series of physicochemical evaluations was performed. Firstly, FTIR spectra were obtained using a Vertex 70 spectrometer (Bruker). Samples were analyzed in the form of tablets, made by pressing a mixture of anhydrous KBr (ca. 0.25 g) and 1 mg of the tested substance in a special steel ring, under a pressure of 10 MPa. The zeta potential of the obtained materials was determined as a function of pH, using a Zetasizer Nano ZS equipped with an autotitrator (Malvern Instruments Ltd., UK), which enables estimation of electrophoretic mobility, and indirectly of the zeta potential, based on laser Doppler velocimetry measurments. The value of the zeta potential was calculated from the Smoluchowski equation. Low-temperature N₂ sorption was also applied. The surface area (A_BET) and mean pore diameter (S_p) were determined using an ASAP 2020 instrument (Micromeritics Instrument Co., USA). The surface area was determined by the multipoint BET (Brunauer–Emmett–Teller) method, using data on adsorption as a function of relative pressure (p/p₀).

2.3 Immobilization of aminoacylase from Aspergillus melleus

Aminoacylase was immobilized on the ZrO₂·SiO₂ materials (raw and carbonyl-grafted ZrO₂·SiO₂) via an adsorption method. The enzyme solution (1, 3 and 7 mg/mL, 0.2 M solution of phosphate buffer (PBS) at pH = 7) was stirred with the support (0.5 g) for 3 h at ambient temperature. The obtained biocatalytic systems were filtered and washed. The quantity (P) of aminoacylase immobilized on the ZrO₂·SiO₂ (raw and carbonyl-grafted) and the immobilization yield (IY) were analyzed using the Bradford method and calculated from Eqs. (1–2):

$$ {\text{P}} = \frac{{\left( {{\text{C}}_{0} - {\text{C}}_{1} } \right) \times {\text{V}}}}{\text{m}} $$

(1)

$$ {\text{IY}} = \frac{{{\text{C}}_{1} }}{{{\text{C}}_{0} }} \times 100\% $$

(2)

where C₀ and C₁ denote the concentration of the enzyme (mg/mL) in solution before and after immobilization respectively, V is the volume of solution (mL), and m is the mass of support (g). Desorption of the immobilized aminoacylase was evaluated over a time of 3 h using phosphate buffer at pH = 7. For this purpose, both ZrO₂·SiO₂ and carbonyl-grafted ZrO₂·SiO₂ were dispersed in PBS solution. After the specified period of time, the efficiency of desorption (D) was evaluated based on the Bradford method and calculated from Eq. (3):

$$ {\text{D}} = \frac{{{\text{C}}_{2} }}{{{\text{C}}_{1} }} \times 100\% $$

(3)

where C₂ and C₁ denote the concentration of the enzyme (mg/mL) in solution before and after desorption respectively.

2.4 Enzyme assay

The catalytic activity is a very important parameter determining the possible use of an enzyme as a catalyst. Aminoacylase catalyzes the asymmetric hydrolysis of N-acetyl-dl-amino acids to l-amino acids and unhydrolyzed N-acetyl-d-amino acids (Fig. 1).

The free and immobilized aminoacylase were used to catalyze the hydrolysis of N-acetyl-l-methionine, N-acetyl-l-cysteine, N-acetyl-dl-serine and N-acetyl-dl-tryptophan to l-methionine, l-cysteine, l-serine and l-tryptophan, respectively. The apparent activity (A_Ap, U/g) of AAM was measured using the colorimetric ninhydrin method, and was defined as the quantity of enzyme which hydrolyzed 1 µmol of l-amino acid per minute, per 1 g of biocatalyst. The release of the product was observed at 570 nm (using a JASCO V650 spectrophotometer, Japan). Additionally, the relative activity (A_R, %) was calculated from Eq. (4):

$$ A_{R} = \frac{{{\text{activity}}\,{\text{of }}\,{\text{immobilized }}\,{\text{AAM}}}}{{{\text{activity}}\,{\text{of}}\,{\text{free}}\,{\text{AAM}}}} \times 100\% $$

(4)

2.5 Evaluation of the stability of free aminoacylase and obtained biocatalytic systems

The effect of temperature (30–70 °C) and pH (4–9) on the catalytic activity of the obtained biocatalytic systems (aminoacylase immobilized on raw and carbonyl-grafted ZrO₂·SiO₂) was examined based on the reaction illustrated in Fig. 1. The storage stability (after 30 days) and reusability (5 cycles) were also evaluated.

3 Results and discussion

3.1 Physicochemical characterization of supports and biocatalytic systems

The first stage of physicochemical evaluation involved infrared spectral analysis. Figure 2 shows the FTIR spectra of the supports, free aminoacylase, and aminoacylase immobilized on ZrO₂·SiO₂ and ZrO₂·SiO₂_GA. The most important features of the ZrO₂·SiO₂ surface (Fig. 2a) include O–H stretching vibrations (between 3200 and 3700 cm⁻¹), deformational vibrations of –OH groups (1629 cm⁻¹) arising from physically adsorbed water, and asymmetric vibrations of Si–O–Si and Zr–O–Si between 1200 and 950 cm⁻¹; the bands at 675–600 cm⁻¹ indicate the presence of Si–O and Zr–O bonds (Ciesielczyk et al. 2018; Rahulan et al. 2013). Additionally, the FTIR spectrum of carbonyl-grafted ZrO₂·SiO₂ contained bands corresponding to –CH and C=O stretching vibrations at 2850 and 1530 cm⁻¹, respectively.

The FTIR spectrum of free aminoacylase from Aspergillus melleus (Fig. 2b) contains a wide range of signals. The band at 3430 cm⁻¹ indicates the presence of hydroxyl groups in the enzyme structure. Close to 2935 cm⁻¹ is a band corresponding to stretching vibrations of –C–H bonds. Important features include the bands at 1652 and 1540 cm⁻¹ corresponding to vibrations of amide I and II bonds, and a peak at 1120 cm⁻¹ generated by stretching vibrations of C–O bonds present in the protein structure.

Figure 2c and d show the FTIR spectra of aminoacylase immobilized on raw and carbonyl-grafted ZrO₂·SiO₂ (ZrO₂·SiO₂_GA). The presence of amide bonds (amide I on the spectrum of aminoacylase immobilized on ZrO₂·SiO₂, and amide I and II on the spectrum of aminoacylase immobilized on ZrO₂·SiO₂_GA) between 1450 and 1630 cm⁻¹ indirectly confirm the effectiveness of the immobilization process. The intensity of amide bond signals increased with increasing concentration of enzyme solution; this is probably associated with the quantity of immobilized enzyme.

The surface charges of the free enzyme and of the support with and without enzyme were determined based on values of the zeta potential as a function of pH (Fig. 3). The ZrO₂·SiO₂ zeta potential values give a high potential in a range from 38 to − 48 mV, in the whole analyzed pH range (2–10). The isoelectric point (IEP) for this sample is 4.1. For the free aminoacylase from Aspergillus melleus the zeta potential value ranges from 10 to − 35 mV, with an isoelectric point of 3.4. The ZrO₂·SiO₂ containing immobilized enzyme (ZrO₂·SiO₂_AAM) has a more negative potential than the raw materials. In this case the zeta potential is negative (between − 10 and − 60 mV) in the whole analyzed pH range.

Modification of ZrO₂·SiO₂ with glutaraldehyde led to a change in the value of the isoelectric point. The IEP for this sample was recorded at pH = 5.7. On the other hand, the zeta potential values for carbonyl-grafted ZrO₂·SiO₂ lie in a similar range (from 35 to − 50 mV in the analyzed pH range) as in case of raw ZrO₂·SiO₂. Immobilization of the enzyme onto carbonyl-grafted ZrO₂·SiO₂ (ZrO₂·SiO₂_GA_AAM) led also to some changes in the zeta potential values calculated for varying pH, as compared with the raw support. The zeta potential for sample ZrO₂·SiO₂_AG_AAM ranged from 20 to − 50 mV. Moreover, a shift in the IEP value (pH = 5.1) for this sample was observed.

The changes in zeta potential after immobilization probably results from differences in the surface charge of the materials, as well as interactions between the enzyme and support (Coutinho et al. 2018). These phenomena may be related to the electrostatic interactions (NH₃⁺, COO⁻, O⁻). The covalent bonds generated between the groups present in the enzyme (–NH₂) and in the modified support (–C=O) are also of great importance. This fact was confirmed by the FTIR analysis. Besides these, the binding may also be supported by hydrophobic interactions and van der Waals interactions (Mehde et al. 2018). Additionally, the immobilization of the enzyme onto ZrO₂·SiO₂ oxide system shifts the slipping plane a little bit stronger and the zeta potential is more negative (Wisniewska et al. 2015; Szewczuk-Karpisz and Wisniewska 2018).

Based on the FTIR and zeta potential analysis, a probable mechanism of immobilization of AAM onto carbonyl-grafted ZrO₂·SiO₂ was proposed (Fig. 4).

The next stage of physicochemical evaluation concerned the influence of the immobilization process on porous structure parameters, such as surface area and pore size (Table 1). Figure 5 presents the nitrogen adsorption/desorption isotherms of the supports ZrO₂·SiO₂ and ZrO₂·SiO₂_GA. The obtained isotherms were classified as type II, and their shape suggests that there exist only mesopores between small particles (Ciesielczyk et al. 2018). The unmodified ZrO₂·SiO₂ has the highest surface area (A_BET = 276 m²/g). The average pore size of this sample is 5.3 nm. Modification of zirconia/silica oxide system with glutaraldehyde caused a significant decrease in surface area (to 194 m²/g), but the average pore size increased slightly (to 6.5 nm) due to incorporation of modifier molecules. The surface area of oxide material decreased after modification with GA, which is probably associated with blocking of the active sites (in this case hydroxyl groups present on the ZrO₂·SiO₂ surface) by the carboxyl group from glutaraldehyde.

Table 1

Porous structure parameters of supports and obtained biocatalytic systems

Sample	A_BET (m²/g)	S_p (nm)
ZrO₂·SiO₂	276	5.3
ZrO₂·SiO₂_AAM	60	2.1
ZrO₂·SiO₂_GA	194	6.5
ZrO₂·SiO₂_GA_AAM	68	2.1

The immobilization process leads to a decrease in the values of the porous structure parameters, which may serve as an indirect indication of the effectiveness of immobilization. This is evidenced by the smaller surface area values (60–68 m²/g) and pore sizes (2.1 nm) as compared with the raw supports. The reduction in the pore size after immobilization is probably associated with the immobilization of enzyme inside the pores and with the blocking of pore spaces (Forde et al. 2010).

The data given in Table 2 show that the quantity of immobilized aminoacylase increases with an increase in the enzyme concentration, reaching maximum values of 745 mg/g (for 7 mg/mL aminoacylase immobilized onto ZrO₂·SiO₂) and 746 mg/g (for 7 mg/mL aminoacylase immobilized onto ZrO₂·SiO₂_GA). The same dependence was observed for immobilization yield, which also increased with increasing concentration of the enzyme, reaching highest values of 99.4–99.6% for both supports. The obtained systems exhibited high stability—desorption of the enzyme did not exceed 0.2%. This is closely related to the efficiency of adsorption of the enzyme and its various interactions with the zirconia/silica oxide system.

Table 2

Quantities of aminoacylase loaded on zirconia/silica oxides (mg/g), immobilization yield (%) and desorption efficiency (%)

Sample	P (mg/g)	IY (%)	D (%)
ZrO₂·SiO₂_AAM_1 mg	49	98.8	0.20
ZrO₂·SiO₂_AAM_3 mg	298	99.2	0.02
ZrO₂·SiO₂_AAM_7 mg	745	99.4	0.01
ZrO₂·SiO₂_GA_AAM_1 mg	49	98.6	0.18
ZrO₂·SiO₂_GA_AAM_3 mg	299	99.6	0.03
ZrO₂·SiO₂_GA_AAM_7 mg	746	99.5	0.01

The obtained biocatalytic systems (ZrO₂·SiO₂_AAM and ZrO₂·SiO₂_GA_AAM) were used as biocatalysts in the hydrolysis of certain N-acetyl-l-amino acids (Tables 2 and 3). Based on this reaction, the catalytic activity of the immobilized aminoacylase was determined. N-acetyl-l-methionine is most often used as a substrate in hydrolysis reactions. Table 3 contains the values of apparent (A_Ap) and relative (A_R) activity obtained for aminoacylase (at concentrations of 1, 3 and 7 mg/mL) immobilized onto unmodified and modified ZrO₂·SiO₂. These data show that apparent and relative activity increased with increasing concentration of aminoacylase. The immobilized aminoacylase retains high relative activity (A_R = 45% for ZrO₂·SiO₂_AAM_7 mg and A_R = 54% for ZrO₂·SiO₂_GA_AAM_7 mg) as compared with the activity of the native enzyme. Aminoacylase immobilized onto carbonyl-grafted ZrO₂·SiO₂ was found to exhibit better catalytic activity. This may be related to the formation of stable bonds between carbonyl groups from the support and amine groups from the enzyme.

Table 3

Catalytic activity of immobilized aminoacylase, evaluated based on the hydrolysis of N-acetyl-l-methionine

Sample	A_Ap (U/g)	A_R (%)
Free AAM	6382	100
ZrO₂·SiO₂_AAM_1 mg	2423	27
ZrO₂·SiO₂_AAM_3 mg	2560	28
ZrO₂·SiO₂_AAM_7 mg	4112	45
ZrO₂·SiO₂_GA_AAM_1 mg	3470	38
ZrO₂·SiO₂_GA_AAM_3 mg	3139	34
ZrO₂·SiO₂_GA_AAM_7 mg	4947	54

Catalytic tests were also performed using other amino acids derivatives (N-acetyl-l-cysteine, -dl-serine and -dl-tryptophan). The results, given in Table 4, show that the aminoacylase immobilized onto ZrO₂·SiO₂ and ZrO₂·SiO₂_GA can also be used to catalyze the synthesis reactions of l-cysteine, dl-serine and dl-tryptophan, although the obtained values of apparent and relative activity are smaller than those presented in Table 3. The values of relative activity for the immobilized enzyme are higher in the synthesis of l-cysteine and l-tryptophan (34% and 28% respectively for ZrO₂·SiO₂_AAM, 22% and 38% for ZrO₂·SiO₂_GA_AAM). This fact may be related to the structure of the amino acids used. In the literature, besides the standard derivative of methionine, N-acetyl-l-theanine has also been used to determine the enzymatic activity of immobilized aminoacylase (Li et al. 2015). In that study the immobilized aminoacylase (on electrospun nanofibrous membrane) had a relative activity of 50%.

Table 4

Catalytic properties of immobilized aminoacylase based on hydrolysis of N-acetyl-l-cysteine, -dl-serine and -dl-tryptophan

Sample	A_Ap (U/g)	A_R (%)
N-acetyl-l-cysteine
Free AAM	14.7	100
ZrO₂·SiO₂_AAM	5.1	34
ZrO₂·SiO₂_GA_AAM	3.3	22
N-acetyl-dl-serine
Free AAM	6.9	100
ZrO₂·SiO₂_AAM	2.2	15
ZrO₂·SiO₂_GA_AAM	1.4	9
N-acetyl-dl-tryptophan
Free AAM	15.4	100
ZrO₂·SiO₂_AAM	4.3	28
ZrO₂·SiO₂_GA_AAM	5.8	38

The last stage of the research involved determination of the influence of pH and temperature on the activity of free and immobilized aminoacylase, in addition to storage stability and reusability. The results are presented in Figs. 6 and 7. Free aminoacylase retains high activity in the pH range 6–8 (activity above 70%) and in the temperature range 40–50 °C (activity above 70%). Below pH = 6 and 40 °C the relative activity rapidly decreases; the same is observed above pH = 8 and 50 °C. The immobilized enzyme, however, exhibits good activity in the whole analyzed pH range and temperature range. Better catalytic activity was observed for aminoacylase immobilized onto carbonyl-grafted ZrO₂·SiO₂, which is probably related to the nature of the bonds formed (covalent bonds) between the enzyme and the support. In this case the immobilized enzyme exhibited activity above 50% in the whole analyzed pH range and activity above 60% in the temperature range 30–60 °C. Aminoacylase immobilized on raw ZrO₂·SiO₂ (ZrO₂·SiO₂_AAM) also retains good activity (above 40%) at pH = 5–9, but the activity of this biocatalytic system is above 60% only in the temperature range from 30 to 50 °C. Above 50 °C the immobilized AAM exhibits practically no activity. Similar findings were reported by Xiao et al. (2006) (acylase immobilized on hollow silica nanotubes) and Pang et al. (2016) (laccase immobilized on a micro-mesoporous Zr-metal organic framework).

The storage stability and reusability of the obtained systems were also investigated, and the results are shown in Fig. 7. The biocatalytic systems retained enzymatic activity after 30 days of storage and after five reaction cycles. The system ZrO₂·SiO₂_GA_AAM has better catalytic properties than ZrO₂·SiO₂_AAM. Aminoacylase immobilized onto ZrO₂·SiO₂_GA retains approximately 85% of its initial activity after 30 days, and 70% after five cycles. This is probably related to the more stable covalent bonds formed between the enzyme and the support.

In summary, the results of the study have shown that immobilization process of aminoacylase onto zirconia/silica oxide systems (ZrO₂·SiO₂ and ZrO₂·SiO₂_GA) was successfully carried out. The strength of the interactions between enzyme and support may be due to covalent bonds. These bonds are probably formed between carbonyl and amino groups, present on the support surface and in the enzyme structure respectively. One of the most important advantages of an immobilized enzyme is its reusability (Zivkovic et al. 2015). Table 5 gives the relative activity after five cycles of various biocatalytic systems. In previous studies the enzymes were immobilized on materials consisting of silica or zirconia only, unlike the combined zirconia/silica systems used in the present study. The data in Table 5 show that enzymes immobilized on silica or zirconia retain only 40–50% of their initial activity. Only one study found that the relative activity of an enzyme immobilized on a silica or zirconia support reached 90%. This is probably related to the immobilization method used or the structure of the enzyme in question (lipase).

Table 5

Comparison of relative activities of enzymes immobilized on zirconia- and silica-based materials

Enzyme	Support	Relative activity after 5 cycles of reaction (%)	References
Acylase	Silica functionalized with amino groups	50	Shah et al. (2008)
Aminoacylase	Amino and carbonyl-grafted silica	40	Kolodziejczak-Radzimska et al. (2018a)
Lipase	ZrO₂-CeO₂	40	Guncheva et al. (2014)
Laccase	Zr-MOF (micro-mesoporous Zr-metal organic framework)	50	Pang et al. (2016)
Lipase	Silica and zirconia	90	Zivkovic et al. (2015)
Aminoacylase	ZrO₂·SiO₂	60	This study
Aminoacylase	ZrO₂·SiO₂ with carbonyl groups	70	This study

4 Conclusion

Aminoacylase from Aspergillus melleus has been successfully immobilized onto raw and carbonyl-grafted ZrO₂·SiO₂. Standard Bradford analysis was performed, in addition to a number of physicochemical techniques, including Fourier transform infrared spectroscopy, laser Doppler velocimetry and low-temperature N₂ sorption, to investigate the effectiveness of the immobilization process. Changes observed in the FTIR spectra and variations in zeta potential are probably caused by differences in the surface conditions of the particles, as well as interactions involving other particles and ions in the solution. Based on all of the analyses, a mechanism has been proposed for the reaction of immobilization of aminoacylase onto carbonyl-grafted ZrO₂·SiO₂, primarily involving electrostatic and covalent interactions. Moreover, it has been shown that aminoacylase immobilized on raw and carbonyl-grafted ZrO₂·SiO₂ can be used as a biocatalyst in the synthesis of amino acids (l-methionine, l-cysteine, l-serine and l-tryptophan). Aminoacylase from Aspergillus melleus immobilized on carbonyl-grafted ZrO₂·SiO₂ was less sensitive to temperature and pH changes than the free enzyme. Furthermore, the immobilized catalyst changes from a homogeneous to a heterogeneous form, which facilitates simple separation of the biocatalytic system from the reaction mixture. Because of this, it was possible to recycle the immobilized aminoacylase and retain 70% of its initial activity over at least five hydrolysis cycles. It should be also highlighted that proposed immobilization technique can be applied to other enzymes. This make it unique because enables preparation of novel, functional biocatalysts characterized with wide range of potential application.

Acknowledgements

This work was supported by the Polish Ministry of Science and Higher Education (Grant No. 03/32/SBAD/0906).

Open AccessThis article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Vorheriger Artikel n-Hexane conversion on γ-alumina supported palladium–platinum catalysts

Nächster Artikel The role of novel lignosulfonate-based sorbent in a sorption mechanism of active pharmaceutical ingredient: batch adsorption tests and interaction study

Abdollahi, K., Yazdani, F., Panahi, R.: Covalent immobilization of tyrosinase onto cyanuric chloride crosslinked amine-functionalized superparamagnetic nanoparticles: synthesis and characterization of the recyclable nanobiocatalyst. Int. J. Biol. Macromol. 94, 396–405 (2017)CrossRefPubMed

Ambrogio, M.W., Thomas, C.R., Zhao, Y.L., Zink, J.I., Stoddart, J.F.: Mechanized silica nanoparticles: a new frontier in theranostic nanomedicine. Acc. Chem. Res. 44, 903–913 (2011)CrossRefPubMedPubMedCentral

Antecka, K., Zdarta, J., Siwińska-Stefańska, K., Sztuk, G., Jankowska, E., Oleskowicz-Popiel, P., Jesionowski, T.: Synergistic degradation of dye wastewaters using binary or ternary oxide systems with immobilized laccase. Catalysts 8, 402–420 (2018)CrossRef

Cai, C., Gao, Y., Liu, Y., Zhong, N., Liu, N.: Immobilization of Candida antarctica lipase B onto SBA-15 and their application in glycerolysis for diacylglycerols synthesis. Food Chem. 212, 205–212 (2016)CrossRefPubMed

Cengiz, S., Cavas, L., Yurdakoc, K.: Bentonite and sepiolite as supporting media: immobilization of catalase. Appl. Clay Sci. 65–66, 114–120 (2012)CrossRef

Chao, C., Liu, J., Wang, J., Zhang, Y., Zhang, B., Zhang, Y., Xiang, X., Chen, R.: Surface modification of halloysite nanotubes with dopamine for enzyme immobilization. Appl. Mater. Interfaces 5, 10559–10564 (2013)CrossRef

Ciesielczyk, F., Goscianska, J., Zdarta, J., Jesionowski, T.: The development of zirconia/silica hybrids for the adsorption and controlled release of active pharmaceutical ingredients. Colloid Surf. A 545, 39–50 (2018)CrossRef

Coutinho, T.C., Rojas, M.J., Tardioli, P.W., Paris, E.C., Farinas, C.S.: Nanoimmobilization of β-glucosidase onto hydroxyapatite. Int. J. Biol. Macromol. 119, 1042–1051 (2018)CrossRefPubMed

Cowana, A., Fernandez-Lafuente, R.: Enhancing the functional properties of thermophilic enzymes by chemical modification and immobilization. Enzyme Microb. Technol. 49, 326–346 (2011)CrossRef

Del Angel-Lopez, D., Torres-Huerta, A.M., Dominguez-Crespo, M.A., Onofre-Bustamante, E.: Effect of ZrO₂:SiO₂ dispersion on the thermal stability, mechanical properties and corrosion behavior of hybrid coatings deposited on carbon steel. J. Alloys Compd. 615, S423–S432 (2015)CrossRef

Das, R., Ranjan, R., Sinha, N., Kayastha, A.M.: Comparative characterization of peanut β-amylase immobilization onto graphene oxide and graphene oxide carbon nanotubes by solid-state NMR. J. Phys. Chem. C 122, 19259–19265 (2018)CrossRef

Demkina, E.V., Shanenko, E.F., Nikolaev, Y.A., El’-Registan, G.I.: Model of the regulation of activity of immobilized enzymes (amylases) in soil. Microbiology 86, 231–240 (2017)CrossRef

Forde, J., Vakurov, A., Gibson, T.D., Millner, P., Whelehan, M., Marison, I.W., O’Fagain, C.: Chemical modification and immobilisation of lipase B from Candida antarctica onto mesoporous silicates. J. Mol. Catal. B 66, 203–209 (2010)CrossRef

Guncheva, M., Paunova, K., Dimitrov, M., Yancheva, D.: Stabilization of Candida rugosa lipase on nanosized zirconia-based materials. J. Mol. Catal. B 108, 43–50 (2014)CrossRef

Haghighi, N., Hallaj, R., Salimi, A.: Immobilization of glucose oxidase onto a novel platform based on modified TiO₂ and graphene oxide, direct electrochemistry, catalytic and photocatalytic activity. Mater. Sci. Eng. 73, 417–424 (2017)CrossRef

Heater, B.S., Lee, M.M., Chan, M.K.: Direct production of a genetically-encoded immobilized biodiesel catalyst. Sci. Rep. 8, 12783–12793 (2018)CrossRefPubMedPubMedCentral

Homaei, A., Sariri, R., Vianello, F.: Enzyme immobilization: an update. J. Chem. Biol. 6, 185–205 (2013)CrossRefPubMedPubMedCentral

Jesionowski, T., Krysztafkiewicz, A.: Influence of silane coupling agents on surface properties of precipitated silicas. Appl. Surf. Sci. 172, 18–32 (2001)CrossRef

Jesionowski, T., Zdarta, J., Krajewska, B.: Enzyme immobilization by adsorption: a review. Adsorption 20, 801–821 (2014)CrossRef

Liang, J., Srinivasan, P.B., Blawert, C., Dietzel, W.: Comparison of electrochemical corrosion behaviour of MgO and ZrO₂ coatings on AM50 magnesium alloy formed by plasma electrolytic oxidation. Corros. Sci. 51, 2483–2492 (2009)CrossRef

Jin, Q., Li, X., Deng, C., Zhang, Q., Yi, D., Wang, X., Tang, Y., Wang, Y.: Silica nanowires with tunable hydrophobicity for lipase immobilization and biocatalytic membrane assembly. J. Colloid Interface Sci. 531, 555–563 (2018)CrossRefPubMed

Klapiszewski, L., Królak, M., Jesionowski, T.: Silica synthesis by the sol-gel method and its use in the preparation of multifunctional biocomposites. Cent. Eur. J. Chem. 12, 173–184 (2014)CrossRef

Kolodziejczak-Radzimska, A.: Functionalized Stober silica as a support in immobilization process of lipase from Candida rugosa. Physicochem. Probl. Miner. Process. 53, 878–892 (2017)

Kolodziejczak-Radzimska, A., Zdarta, J., Jesionowski, T.: Physicochemical and catalytic properties of acylase I from Aspergillus melleus immobilized on amino- and carbonyl-grafted Stober silica. Biotech. Progress 34, 767–777 (2018a)CrossRef

Kolodziejczak-Rdzimska, A., Zdarta, J., Ciesielczyk, F., Jesionowski, T.: An organofunctionalized MgO·SiO₂ hybrid support and its performance in the immobilization of lipase from Candida rugosa. Korean J. Chem. Eng. 35, 2220–2231 (2018b)CrossRef

Li, J., Zhao, Z., Mo, T., Wang, L., Li, P.: Immobilization of aminoacylase on electrospun nanofibrous membrane for the resolution of dl-theanine. J. Mol. Catal. B 116, 24–28 (2015)CrossRef

Masuda, Y., Kugimiya, S., Kato, K.: Improvement of thermal-stability of enzyme immobilized onto mesoporous zirconia. J. Asian Ceram. Soc. 2, 11–19 (2014)CrossRef

Mateo, C., Palomo, J., Fernandez-Lorente, G.: Improvement of enzyme activity, stability and selectivity via immobilization techniques. Enzyme Microb. Technol. 40, 1451–1463 (2007)CrossRef

Mehde, A.A., Mehdi, W.A., Severgun, O., Cakar, S., Ozacar, M.: Lipase-based on starch material as a development matrix with magnetite cross-linked enzyme aggregates and its application. Int. J. Biol. Macromol. 120, 1533–1543 (2018)CrossRefPubMed

Mohiuddin, M., Arbain, D., Islam, A.K.M.S., Rahman, M., Ahmad, M.S., Ahmad, M.N.: Covalent immobilization of α-glucosidase enzyme onto amine functionalized multi-walled carbon nanotubes. Curr. Nanosci. 5, 730–735 (2014)CrossRef

Noori, N., Nikoorazm, M., Ghorbani-Choghamarani, A.: Oxo-vanadium immobilized on l-cysteine-modified MCM-41 as catalyst for the oxidation of sulfides and oxidative coupling of thiols. Microporous Mesoporous Mater. 234, 166–175 (2016)CrossRef

Pang, S., Wu, Y., Zhang, X., Li, B., Ouyang, J., Ding, M.: Immobilization of laccase via adsorption onto bimodal mesoporous Zr-MOF. Process Biochem. 51, 229–239 (2016)CrossRef

Piccinini, E., Bliem, C., Rozman, C.R., Battaglini, F., Azzaroni, O., Knoll, W.: Enzyme-polyelectrolyte multilayer assemblies on reduced graphene oxide field-effect transistors for biosensing applications. Biosens. Bioelectron. 92, 661–667 (2017)CrossRefPubMed

Pogorilyi, R.P., Pylypchuk, I., Melnyk, I.V., Zub, Y.L., Seisenbaeva, G.A., Kessler, V.G.: Sol-gel derived adsorbents with enzymatic and complexonate functions for complex water remediation. Nanomaterials 7, 298–315 (2017)CrossRefPubMedCentral

Pylypchuk, I.V., Kessler, V.G., Seisenbaeva, G.A.: Simultaneous removal of acetaminophen, diclofenac, and Cd(II) by Trametes versicolor laccase immobilized on Fe3O4/SiO2-DTPA hybrid nanocomposites. ACS Sustain. Chem. Eng. 6, 9979–9989 (2018)CrossRef

Rahulan, K.M., Vinitha, G., Stephen, D.L, Kanakam, C.C.: Synthesis and optical limiting effects in ZrO₂ and ZrO₂@SiO₂ core shell nanostructures. Ceram. Int. 39, 5281–5286 (2013)CrossRef

Santos, M., Lobo, I., Cruz, R.: Synthesis and characterization of novel ZrO₂∙SiO₂ mixed oxides. Mater. Res. 17, 700–707 (2014)CrossRef

Shah, P., Sridevi, N., Prabhune, A., Ramaswamy, V.: Structural features of Penicillin acylase adsorption on APTES functionalized SBA-15. Microporous Mesoporous Mater. 116, 157–165 (2008)CrossRef

Shibli, S.M.A., Chacko, F., Divya, C.: Al₂O₃–ZrO₂ mixed oxide composite incorporated aluminium rich zinc coatings for high wear resistance. Corros. Sci. 52, 518–525 (2010)CrossRef

Szewczuk-Karpisz, K., Wisniewska, M.: Lysozyme as a flocculant-inducing agent improving the silica removal from aqueous solutions - a turbidimetric study. J. Environ. Manage. 226, 187–193 (2018)CrossRefPubMed

Tak, M., Gupta, V., Tomar, M.: A highly efficient urea detection using flower-like zinc oxide nanostructures. Mater. Sci. Eng., C 57, 38–48 (2017)CrossRef

Vaizogullar, A., Balci, A., Ugurlu, M.: Synthesis of ZrO₂ and ZrO₂/SiO₂ particles and photocatalytic degradation of methylene blue. Indian J. Chem. 54, 1434–1439 (2015)

Wisniewska, M., Ostolska, I., Szewczuk-Karpisz, K., Chibowski, S., Terpiłowski, K., Gunko, V.M., Zarko, V.I.: Investigation of the polyvinyl alcohol stabilization mechanism and adsorption properties on the surface of ternary mixed nanooxide AST 50 (Al₂O₃–SiO₂–TiO₂). J. Nanoparticle Res. 17, 1–14 (2015)CrossRef

Wu, H., Liang, Y., Shi, J.: Enhanced stability of catalase covalently immobilized on functionalized titania submicrospheres. Mater. Sci. Eng. 33, 1438–1445 (2013)CrossRef

Wu, F., Su, L., Yu, P., Mao, L.: Role of organic solvents in immobilizing fungus laccase on single-walled carbon nanotubes for improved current response in direct bioelectrocatalysis. J. Am. Chem. Soc. 139, 1565–1574 (2017)CrossRefPubMed

Xiao, Q.G., Tao, X., Zhang, J.P., Chen, J.F.: Hollow silica nanotubes for immobilization of penicillin G acylase enzyme. J. Mol. Cat. B 42, 14–19 (2006)CrossRef

Xiao, Y.F., Yao, Z., Wang, H.Q., Xiong, Q., Hu, G.M., Xu, H., Wei, P.: Enzymatic synthesis of S-bzl-γ-glutamyl-l-cysteine with γ-glutamyltranspeptidase immobilized onto ordered mesoporous TiO₂. Chin. J. Chem. Eng. 10, 1175–1180 (2010)

Zdarta, J., Meyer, A.S., Jesionowski, T., Pinelo, M.: A general overview of support materials for enzyme immobilization: characteristics, properties, practical utility. Catalysts 8, 92–119 (2018)CrossRef

Zdarta, J., Salek, K., Kolodziejczak-Radzimska, A., Siwinska-Stefanska, K., Szwarc-Rzepka, K., Norman, M., Klapiszewski, Ł., Bartczak, P., Kaczorek, E., Jesionowski, T.: Immobilization of Amano Lipase A onto Stöber silica surface: process characterization and kinetic studies. Open Chem. 13, 138–148 (2015)

Zhai, R., Zhang, B., Liu, L., Xie, Y., Zhang, H., Liu, J.: Immobilization of enzyme biocatalyst on natural halloysite nanotubes. Catal. Commun. 12, 259–263 (2010)CrossRef

Zivkovic, L.T.I., Zivkovic, L.S., Babic, B.M., Kokunesoski, M.J., Jokic, B.M., Karadzic, I.M.: Immobilization of Candida rugosa lipase by adsorption onto biosafe meso/macroporous silica and zirconia. Biochem. Eng. J. 93, 73–83 (2015)CrossRef

Zivkovic, L.T.I., Zivkovic, L.S., Beskoskic, V.P., Gopcevica, K.R., Jokic, B.M., Radosavljevice, D.S., Karadzica, I.M.: The Candida rugosa lipase adsorbed onto titania as nano biocatalyst with improved thermostability and reuse potential in aqueous and organic media. J. Mol. Catal. B 133, 533–542 (2016)CrossRef

Titel: A novel biocatalytic system obtained via immobilization of aminoacylase onto sol–gel derived ZrO2·SiO2 binary oxide material: physicochemical characteristic and catalytic activity study
verfasst von: Agnieszka Kołodziejczak-Radzimska
Filip Ciesielczyk
Teofil Jesionowski
Publikationsdatum: 20.04.2019
Verlag: Springer US
Erschienen in: Adsorption / Ausgabe 4/2019
Print ISSN: 0929-5607
Elektronische ISSN: 1572-8757
DOI: https://doi.org/10.1007/s10450-019-00085-7

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Publisher's Note

1 Introduction

2 Materials and methods

2.1 Materials

2.2 Synthesis, modification and characterization of ZrO2·SiO2

2.3 Immobilization of aminoacylase from Aspergillus melleus

2.4 Enzyme assay

2.5 Evaluation of the stability of free aminoacylase and obtained biocatalytic systems

3 Results and discussion

3.1 Physicochemical characterization of supports and biocatalytic systems

4 Conclusion

Acknowledgements

Publisher's Note

Weitere Artikel der Ausgabe 4/2019

Experimental evaluation of simulated moving bed reactor for transesterification reaction synthesis of glycol ether ester

Investigation of CO2 capture using acetate-based ionic liquids incorporated into exceptionally porous metal–organic frameworks

Adsorption selectivity of heavy metals by Na-clinoptilolite in aqueous solutions

Impact of water activity on double layer parameters at the mercury/chlorates(VII) interface in the presence of mixed adsorption layers of 6-mercaptopurine–Triton X-100

Measuring adsorption isotherms with a flowmeter and a pressure gauge

n-Hexane conversion on γ-alumina supported palladium–platinum catalysts

Premium Partner

Marktübersichten

2.2 Synthesis, modification and characterization of ZrO₂·SiO₂