26.04.2017 | Original Paper

Preparation of silver/carbon fiber/polyaniline microwave absorption composite and its application in epoxy resin

verfasst von: Bo Cheng, Jin Wang, Fan Zhang, Shuhua Qi

Erschienen in: Polymer Bulletin | Ausgabe 1/2018

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

Microwave absorbing Ag/CF/polyaniline (PANI) composites with PANI particles evenly wrapped on the surface of the silver-plated carbon fiber, were prepared via in situ polymerization. The obtained composite was analyzed by SEM, XRD, TGA, four probes resistance tester and a vector network analyzer. The results indicated that silver nanoparticles were deposited on the surface of CF uniformly and Ag/CF was completely wrapped by PANI particles. Ag/CF/PANI composite with conductivity of 2.16 S/cm displayed better thermal stability than that of PANI. Meanwhile, Ag/CF/PANI composite with microwave reflection loss up to −13.2 dB at 9.3 GHz at thickness of 2.0 mm outperformed that of PANI matrix and CF/PANI composite. The epoxy matrix composite with Ag/CF/PANI dispersed inside homogenously performed −8 dB at 4.5 wt% loading content.

Vorheriger Artikel Ring opening polymerization of ε-caprolactone using sterically bulky salicylaldimine Zn complexes

Nächster Artikel Curable precursors derived from chemical recycling of poly(ethylene terephthalate) and polylactic acid and physical properties of their thermosetting (co)polyesters

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Gerasimov EG, Mushnikov NV, Inishev AA, Terentev PB, Gaviko VS (2016) Structure, magnetic and magnetothermal properties of the non-stoichiometric ErCo₂Mn_x alloys. J Alloys Compd 680:359–365. doi:10.1016/j.jallcom.2016.04.130 CrossRef

Schaarschmidt A, Farah AA, Aby A, Helmy AS (2009) Influence of nonadiabatic annealing on the morphology and molecular structure of PEDOT–PSS films. J Phys Chem B 113(28):9352–9355. doi:10.1021/jp904147v CrossRef

Sun G, Dong B, Cao M, Wei B, Hu C (2011) Hierarchical dendrite-like magnetic materials of Fe₃O₄, γ-Fe₂O₃, and Fe with high performance of microwave absorption. Chem Mater 23(6):1587–1593. doi:10.1021/cm103441u CrossRef

Xu J, Wang K, Zu SZ, Han B, Wei Z (2010) Hierarchical nanocomposites of polyaniline nanowire arrays on graphene oxide sheets with synergistic effect for energy storage. ACS Nano 4(9):5019–5026. doi:10.1021/nn1006539 CrossRef

Li JH, Da HF, Qian Liu, Liu SF (2006) Preparation of sulfur-free expanded graphite with 320 μm mesh of flake graphite’. Mater Lett 60:3927–3930. doi:10.1016/j.matlet.2006.06.066 CrossRef

Zhao Y, Liu J, Hu Y, Cheng H, Hu C, Jiang C, Jiang L, Cao A, Qu L (2013) Highly compression-tolerant supercapacitor based on polypyrrole-mediated graphene foam electrodes. Adv Mater 25(4):591–595. doi:10.1002/adma.201203578 CrossRef

Xie ZL, Huang X, Titirici MM, Taubert A (2014) Mesoporous graphite nanoflakes via ionothermal carbonization of fructose and their use in dye removal. RSC Adv 4(70):37423–37430. doi:10.1039/C4RA05146G CrossRef

Zhu YF, Zhang L, Natsuki T, Fu YQ, Ni QQ (2012) Facile synthesis of BaTiO₃ nanotubes and their microwave absorption properties. ACS Appl Mater Interfaces 4(4):2101–2106. doi:10.1021/am300069x CrossRef

Deng L, Han M (2007) Microwave absorbing performances of multiwalled carbon nanotube composites with negative permeability. Appl Phys Lett 91(2):3119. doi:10.1063/1.2755875 CrossRef

10.

Benykhlef S, Bekhoukh A, Berenguer R, Benyoucef A, Morallon E (2015) PANI-derived polymer/Al₂O₃ nanocomposites: synthesis, characterization, and electrochemical studies. Colloid Polym Sci 294(12):1877–1885. doi:10.1007/s00396-016-3955-y CrossRef

11.

Chouli F, Radja I, Morallon E, Benyoucef A (2015) A novel conducting nanocomposite obtained by p-anisidine and aniline with titanium (IV) oxide nanoparticles: synthesis, characterization, and electrochemical properties. Polym Compos. doi:10.1002/pc.23837

12.

Dahou FZ, Khaldi MA, Zehhaf A, Benyoucef A, Ferrahi MI (2015) Nanocomposite of 2-aminophenol with aniline using copper-montmorillonite: synthesis, characterization, conductivity, and electrochemical study. Adv Polym Tech 35(4):411–418. doi:10.1002/adv.21566 CrossRef

13.

Radja I, Djelad H, Morallon E, Benyoucef A (2015) Characterization and electrochemical properties of conducting nanocomposites synthesized from p-anisidine and aniline with titanium carbide by chemical oxidative method. Synth Met 202:25–32. doi:10.1016/j.synthmet.2015.01.028 CrossRef

14.

Ketpang K, Park JS (2010) Electrospinning PVDF/PPy/MWCNTs conducting composites. Synth Met 160(15):1603–1608. doi:10.1016/j.synthmet.2010.05.022 CrossRef

15.

Khaldi M, Benyoucef A, Quijada C, Yahiaoui A, Morallon E (2014) Synthesis, characterization and conducting properties of nanocomposites of intercalated 2-aminophenol with aniline in sodium-montmorillonite. J Inorg Organomet Polym 24(2):267–274. doi:10.1007/s10904-01-9998-3 CrossRef

16.

Chouli F, Zehhaf A, Benyoucef A (2014) Preparation and characterization of the new conducting composites obtained from 2-methylaniline and aniline with activated carbon by in situ intercalative oxidative polymerization. Macromol Res 22(1):26–31. doi:10.1007/s13233-014-2005-1 CrossRef

17.

Zhan J, Yao Y, Zhang C, Li C (2014) Synthesis and microwave absorbing properties of quasione-dimensional mesoporous NiCo₂O₄ nanostructure. J Alloys Comp 585:240–244. doi:10.1016/j.jallcom.2013.09.091 CrossRef

18.

Qing YC, Wen QL, Fa L, Zhou W, Zhu D (2016) Graphene nanosheets/BaTiO₃ ceramics as highly efficient electromagnetic interference shielding materials in the X-band. J Mater Chem C 4(2):371–375. doi:10.1039/C5TC03035H CrossRef

19.

Kuo HM, Hsui TF, Tuo YS, Yuan CL (2012) Microwave adsorption of core–shell structured Sr (MnTi)_xFe_12-2xO₁₉/PANI composites. J Mater Sci 47(5):2264–2270. doi:10.1007/s10853-011-6038-y CrossRef

20.

Qing Y, Min D, Zhou Y, Luo F, Zhou W (2015) Graphene nanosheet-and flake carbonyl iron particle-filled epoxy–silicone composites as thin–thickness and wide-bandwidth microwave absorber. Carbon 86:98–107. doi:10.1016/j.carbon.2015.01.002 CrossRef

21.

Wu Y, Luo H, Wang H (2014) Synthesis of iron (III)-based metal–organic framework/graphene oxide composites with increased photocatalytic performance for dye degradation. RSC Adv 4(76):40435–40438. doi:10.1039/C4RA07566H CrossRef

22.

Wang W, Paudel NR, Yan Y, Duarte F, Mount M (2016) PEDOT: PSS as back contact for CdTe solar cells and the effect of PEDOT: PSS conductivity on device performance. J Mater Sci: Mater Electron 27(2):1057–1061. doi:10.1007/s10854-015-3850-1

23.

Xia F, Liu J, Gu D, Zhao P, Zhang J, Che R (2011) Microwave absorption enhancement and electron microscopy characterization of BaTiO₃ nano-torus. Nanoscale 3(9):3860–3867. doi:10.1039/C1NR10606F CrossRef

24.

Paek SM, Yoo EJ, Honma I (2008) Enhanced cyclic performance and lithium storage capacity of SnO₂/graphene nanoporous electrodes with three-dimensionally delaminated flexible structure. Nano Let 9(1):72–75. doi:10.1021/nl802484w CrossRef

25.

Bose S, Kuila T, Uddin ME, Kime NH, Laua AKT, Lee JH (2010) In-situ synthesis and characterization of electrically conductive polypyrrole/graphene nanocomposites. Polymer 51(25):5921–5928. doi:10.1016/j.polymer.2010.10.014 CrossRef

26.

Chen T, Deng F, Zhu J, Chen C, Sun G, Ma S, Yang X (2012) Hexagonal and cubic Ni nanocrystals grown on graphene: phase-controlled synthesis, characterization and their enhanced microwave absorption properties. J Mater Chem 22(30):15190–15197. doi:10.1039/C2JM31171B CrossRef

27.

Li X, Yi H, Zhang J, Feng J, Li F, Xue D, Zhang H, Peng Y, Mellors NJ (2013) Fe₃O₄–graphene hybrids: nanoscale characterization and their enhanced electromagnetic wave absorption in gigahertz range. J Nanopart Res 15(3):1–11. doi:10.1007/s11051-013-1472-1

28.

Vaisman L, Wagner HD, Marom G (2006) The role of surfactants in dispersion of carbon nanotubes. Adv Colloid Interface Sci 128:37–46. doi:10.1016/j.cis.2006.11.007 CrossRef

29.

Thomassin JM, Vuluga D, Alexandre M, Jérôme C, Molenberg I, Huynen I, Detrembleur C (2012) A convenient route for the dispersion of carbon nanotubes in polymers: application to the preparation of electromagnetic interference (EMI) absorbers. Polymer 53(1):169–174. doi:10.1016/j.polymer.2011.11.026 CrossRef

30.

Ai L, Huang H, Chen Z, Wei X, Jiang J (2010) Activated carbon/CoF₂O₄ composites: facile synthesis, magnetic performance and their potential application for the removal of malachite green from water. Chem Eng J 156(2):243–249. doi:10.1016/j.cej.2009.08.028 CrossRef

31.

Xu X, Deng C, Gao M, Yu W, Yang P, Zhang X (2006) Synthesis of magnetic microspheres with immobilized metal ions for enrichment and direct determination of phosphopeptides by matrix-assisted laser desorption ionization mass spectrometry. Adv Mater 18(24):3289–3293. doi:10.1002/adma.200601546 CrossRef

32.

Wang DW, Li F, Lu GQ, Cheng HM (2008) Synthesis and dye separation performance of ferromagnetic hierarchical porous carbon. Carbon 46(12):1593–1599. doi:10.1016/j.carbon.06.052 CrossRef

Titel: Preparation of silver/carbon fiber/polyaniline microwave absorption composite and its application in epoxy resin
verfasst von: Bo Cheng
Jin Wang
Fan Zhang
Shuhua Qi
Publikationsdatum: 26.04.2017
Verlag: Springer Berlin Heidelberg
Erschienen in: Polymer Bulletin / Ausgabe 1/2018
Print ISSN: 0170-0839
Elektronische ISSN: 1436-2449
DOI: https://doi.org/10.1007/s00289-017-2035-x

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Weitere Artikel der Ausgabe 1/2018

Flexible and free-standing films containing cobalt-doped nanocrystalline zinc oxide dispersed in polyvinylidene fluoride matrix: synthesis and characterization

Synthesis and characterization of zein-based superabsorbent hydrogels and their potential as heavy metal ion chelators

Bio-based poly(pentamethylene oxamide) synthesized by spray/solid-state polycondensation

Physical properties of poly[(thiophene-2,5-diyl)-co-para-chloro benzylidene] doped with cobalt sulphate: synthesis and characterization

Investigation of mechanical and thermal properties of the cetyltrimethylammonium bromide functionalized molybdenum disulfide (MoS2)/epoxy composites

Modification of epoxy resin by silane-coupling agent to improve tensile properties of viscose fabric composites

Premium Partner

Marktübersichten